Effect of filler size and filler loading on wear of experimental flowable resin composites
نویسندگان
چکیده
منابع مشابه
Effect of filler size and filler loading on wear of experimental flowable resin composites
The relationship between wear resistance and filler size or filler loading was clarified for the universal resin composite; however, their relationship in flowable resin composites has not been clarified. The purpose of this study was to investigate the effect of filler size and filler loading on wear of experimental flowable resin composites by using a cyclic loading device. Nine experimental ...
متن کاملEffect of filler content of flowable composites on resin-cavity interface.
The purpose of this in vitro study was to evaluate marginal integrity and wall adaptation in 1- and 2-mm-deep cavities restored with a high filler-loaded flowable composite in comparison to a flowable composite with lower filler content and a conventional hybrid composite. 1-mm-deep dentin and 2-mm-deep enamel-dentin Class I cavities were prepared and restored with a self-etch adhesive and with...
متن کاملEffect of Filler Size and Temperature on Packing Stress and Viscosity of Resin-composites
UNLABELLED The objective of this study was to investigate the effect of filler size on the packing stress and viscosity of uncured resin-composite at 23 °C and 37 °C. A precision instrument used was designed upon the penetrometer principle. Eight resin-composite materials were tested. Packing-stress ranged from 2.60 to 0.43 MPa and viscosity ranged from 2.88 to 0.02 MPa.s at 23 °C. Values for b...
متن کاملShrinkage behaviour of flowable resin-composites related to conversion and filler-fraction.
OBJECTIVES To evaluate the shrinkage-strain, degree of conversion (DC) and percent filler of a range of flowable resin-composites. METHODS Several commercially available flowable resin-composites were selected. The bonded-disk technique was used to measure shrinkage-strain kinetics. Measurements were obtained continuously for 60min by irradiation for 40s at 750mW/cm(2) at two initial temperat...
متن کاملEffects of monomer composition and original filler content on filler loading in the resulting centrifuged composites.
This study examined the effects of monomer composition, original filler content, and application of centrifugal force on the resulting filler loading of composites. Either Bis-MPEPP or UDMA was mixed with TEGDMA at a molar ratio of 1 : 1. Silane-treated silica (14-20 wt%) was added to each mixture. After the mixtures were centrifuged and light-polymerized, rate of increase was determined as the...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Applied Oral Science
سال: 2018
ISSN: 1678-7765,1678-7757
DOI: 10.1590/1678-7757-2016-0652