Effect of equal channel angular pressing on AZ31 wrought magnesium alloys
نویسندگان
چکیده
منابع مشابه
Characteristics of Cavitation in a Superplastic Magnesium Az31 Alloy Processed by Equal- Channel Angular Pressing
Experiments were conducted on a magnesium AZ31 alloy to evaluate the role of cavitation in high temperature superplasticity. Samples were processed by equal-channel angular pressing (ECAP) and then pulled to failure in tension at a temperature of 623K. Similar tests were also conducted on the as-received alloy. The results show the development of significant internal cavitation in this alloy wh...
متن کاملSize effect in equal channel angular pressing (ECAP) process
The influence of the sample size (diameter while keeping the length constant) in equal channel angular pressing (ECAP) of pure aluminum is examined using finite element method (FEM) and experiment. Different sized aluminum rods were processed via ECAP and the effect of sample size on the strain homogeneity, process load, and the ratio of the friction to the total force were evaluated. The resul...
متن کاملRe-strengthening in AA6063 Alloy During Equal Channel Angular Pressing
Equal channel angular pressing (ECAP) is carried out using two different configurations for the exit channel of the ECAP die, i.e., relieved and choked, with angles of 0.2 °. It is found that using a die with relieved exit channel, the sample was extruded for 6 passes with no surface cracks and an average cell size of 727 nm and a fraction of high angle grain boundaries of 54 % were achieved. M...
متن کاملEffect of Equal Channel Angular Pressing and Annealing Treatment on the Evolution of Microstructure in AlMg0.7Si Aluminum Alloy
In this research, samples of AlMg0.7Si aluminum alloy are deformed up to three passes using equal channel angular pressing (ECAP). Formation of a sub-micron structure after three passes of ECAP is demonstrated. Microstructural stability of the samples is investigated at temperatures of 300-500 °C. At 300 °C, fine recrystallized structure forms after 10 min which remains stable when the ...
متن کاملHigh Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing
Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstruct...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Magnesium and Alloys
سال: 2013
ISSN: 2213-9567
DOI: 10.1016/j.jma.2013.11.007