Effect of Dispersed Particle Size on Mechanical Properties of Alumina/Non-Oxides Composites
نویسندگان
چکیده
منابع مشابه
Study of milling effect on particle size and mechanical properties of WC-Co composite
The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratios by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350°C at a rate of temperature rise 50°C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly...
متن کاملStudy of milling effect on particle size and mechanical properties of WC-Co composite
The effect of milling on the particle size and mechanical properties Tungsten Carbide - Cobalt composite were investigated. First, raw materials ratios by mechanical milling for 4 hours at 300 rpm were mixed. The powder in the optimum temperature 1350°C at a rate of temperature rise 50°C / min and shelf life of 4 minutes and the pressure MPa 30 were sintered in SPS. The results indicated nearly...
متن کاملEffect of Particle Size on the Mechanical and Electrical Properties of Epoxy/Spherical Silica Composites
Copyright 2013 KIEEME. All rights reserved. This is an open-access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0) which permits unrestricted noncommercial use, distribution, and reproduction in any medium, provided the original work is properly cited. pISSN: 1229-7607 eISSN: 2092-7592 DOI: http://dx...
متن کاملEffect of Particle Size on the Structural and Mechanical Properties of Al–AlN Nanocomposites Fabricated by Mechanical Alloying
Nanostructured Al composites with 2.5 wt.% aluminum nitride (AlN) were fabricated by powder metallurgy using mechanically milled aluminum powder mixed in a planetary ball mill with different particle sizes of AlN (50 nm and 1 μm) as reinforcement. After 20 h milling, the powders were die-pressed uniaxially in a steel die and then sintered at 670 °C for 2 h. The morphologies and properties of th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 1993
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.101.889