Effect of Al–Zn Alloy Coating on Corrosion Fatigue Behavior of X80 Riser Steel
نویسندگان
چکیده
منابع مشابه
Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with t...
متن کاملEffect of Heat Treatment on Fatigue Behavior of (A193-51T-B7) Alloy Steel
This research comprises a study of the effect of heat treatment on fatigue behavior of (A193-51T-B7) alloy steel. Two heat treatment processes were conducted, namely, annealing and quenching followed by tempering at 200C. All fatigue tests were carried out using a rotary bending machine with constant stress ratio, R=-1. The eddy current probe was used to measure the crack length propagation. Fr...
متن کاملeffect of oral presentation on development of l2 learners grammar
this experimental study has been conducted to test the effect of oral presentation on the development of l2 learners grammar. but this oral presentation is not merely a deductive instruction of grammatical points, in this presentation two hypotheses of krashen (input and low filter hypotheses), stevicks viewpoints on grammar explanation and correction and widdowsons opinion on limited use of l1...
15 صفحه اولthe effect of explicit teaching of metacognitive vocabulary learning strategies on recall and retention of idioms
چکیده ندارد.
15 صفحه اولCorrosion of Cold Spray Deposited Copper Coating on Steel Substrates
The corrosion behavior of copper cold spray coatings on a carbon steel substrate was compared to that of commercially available wrought copper under the conditions anticipated in a nuclear waste repository. Corrosion potential and linear polarization resistance measurements were conducted over 90 d to 120 d in 3.0 mol/L NaCl under anoxic (1) and oxygenated-toanoxic (2) conditions to simulate th...