Effect of airborne particle abrasion protocols on surface topography of Y-TZP ceramic
نویسندگان
چکیده
منابع مشابه
Evaluation of air-particle abrasion of Y-TZP with different particles using microstructural analysis.
BACKGROUND This study evaluated the effect of air-particle abrasion with different particle sizes on the surface roughness and phase transformation of yttria-stabilized tetragonal zirconia ceramics (Y-TZP). METHODS Eighty-four Y-TZP discs of 15 mm diameter and 1.0 mm thickness were fabricated. The samples were divided into four groups (n = 21): (1) air-particle abrasion with 30 μm CoJet sand ...
متن کاملeffect of sub-grid scales on large eddy simulation of particle deposition in a turbulent channel flow
چکیده ندارد.
15 صفحه اولeffect of oral presentation on development of l2 learners grammar
this experimental study has been conducted to test the effect of oral presentation on the development of l2 learners grammar. but this oral presentation is not merely a deductive instruction of grammatical points, in this presentation two hypotheses of krashen (input and low filter hypotheses), stevicks viewpoints on grammar explanation and correction and widdowsons opinion on limited use of l1...
15 صفحه اولEffect of Sintering Profiles on the Properties and Ageing Resistance of Y-tzp Ceramic
A commercially available Y-TZP ceramic powder was fabricated under four different sintering profiles in order to investigate the effects of conventional single-stage sintering (SSS) with dwell times of 1 min and 2 h, respectively, compared with two-stage sintering (TSS), on the physical and mechanical properties of Y-TZP. Sintering was performed up to 1400 o C at a ramp rate of 10 o C/min. It w...
متن کاملEffect of Grinding and Resintering on the Fatigue Limit and Surface Characterization of a Y-TZP Ceramic.
This study evaluated the effect of grinding protocols and resintering on flexural fatigue limit and surface characterization of LavaTM Y-TZP. Bar-shaped specimens (20×4.0×1.2 mm, n=40; 20×4.0×1.5 mm, n=80) were obtained. Half of the thinner specimens (1.2 mm) constituted the as-sintered group (AS), while the thicker ones (1.5 mm) were ground with diamond burs under irrigation (WG) or not (G). T...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Cerâmica
سال: 2012
ISSN: 0366-6913
DOI: 10.1590/s0366-69132012000200017