Effect of Aging Heat Treatment on Corrosion Fatigue Crack Propagation of 7075 Aluminum Alloy
نویسندگان
چکیده
منابع مشابه
Accelerated Threshold Fatigue Crack Growth Effect – Powder Metallurgy Aluminum Alloy
Fatigue crack growth (FCG) research conducted in the near threshold regime has identified a room temperature creep crack growth damage mechanism for a fine grain powder metallurgy (PM) aluminum alloy (8009). At very low ∆K, an abrupt acceleration in room temperature FCG rate occurs at high stress ratio (R = Kmin/Kmax). The near threshold accelerated FCG rates are exacerbated by increased levels...
متن کاملEFFECT OF T6 HEAT TREATMENT ON MECHANICAL PROPERTIES OF CERAMIC REINFORCED CASTED ALUMINUM ALLOY
Aluminium base alloy (Al-Cu-Si) was reinforced with silicon carbide (SiC) particles, in various percentage compositions from 0-20 wt%. Silicon carbide particle size of 20µm was selected. The molten slurry of SiC reinforced base aluminium metal was casted through green and dry sand casting methods and solidification process was carried out under ambient conditions. A selected population...
متن کاملThe Effect of Atmospheric Corrosion on Environmental Fatigue Crack Propagation and Its Inhibition
Age-hardenable aluminum alloys used in aerospace structures are susceptible to environment assisted fatigue crack propagation (EFCP). There has been no controlled examination of thin film electrolyte, typically produced by atmospheric exposures, effects on EFCP or inhibition of such cracking. The goal of this research is to understand EFCP and inhibition for atmospheric conditions of important ...
متن کاملThe Effect of Creep Aging on the Fatigue Fracture Behavior of 2524 Aluminum Alloy
Normal temperature tensile and fatigue tests were adopted to test the mechanical performance and fatigue life of 2524 aluminum alloy under the three states of T3, artificial aging, and creep aging, and scanning electron microscope and transmission electron microscope were also used to observe the fatigue fracture morphology and aging precipitation features of the alloy under the above three sta...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: CORROSION ENGINEERING
سال: 1983
ISSN: 0010-9355,1884-1155
DOI: 10.3323/jcorr1974.32.8_448