Dynamic Strain Aging and the Wire Drawing of Low Carbon Steel Rods.
نویسندگان
چکیده
منابع مشابه
Static Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملstatic strain aging behavior of low carbon steel drawn wire
the static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. to do so, the wires are austenitized at different temperatures and cooled in different rates. then the wires are drawn and aged at a specific temperature and time. before and after aging of each...
متن کاملRecrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has b...
متن کاملan investication into the strain aging of low carbon steels
in this paper, the effect of prestrain on strain aging of low carbon steels, in the temperatures of 100°c and 200°c and the aging time of 50 minutes, and also the effect of aging temperature on strain aging in a constant aging time and prestrain, are investigated. the results of experiments show that with increasing the amount of prestrain, the increase in yield stress and ultimate tensile stre...
متن کاملDeveloping Very Fine Nanopearlitic Structure in a High Carbon Steel Wire before Drawing
The effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. In this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. The results were the minimum interlamellar spacing of 35 nm and maximum ulti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISIJ International
سال: 1995
ISSN: 0915-1559
DOI: 10.2355/isijinternational.35.1532