Dynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملEffect of Composition on the Recrystallization Behavior of if Steels During Simulated Hot Strip Rolling
Flow curves are generated in muti-pass torsion tests for a titanium stabilized and a niobium stabilized IF steel. Two types of test schedule are used, one based on plate rolling and the other approximating strip rolling. The purpose of the former is to define the three critical temperatures of steel rolling. The strip schedules are varied in order to investigate the influence of increasing the ...
متن کاملCoiler Control in Endless Hot Strip Rolling
JFE Steel Corporation’s East Japan Works (Chiba District) started operation of No.3 Hot Strip Mill in 1995. This line was the first in the world to achieve “endless hot strip rolling.” A new Coiler Control technology was developed. Copyright 2005 IFAC
متن کاملDynamic Recrystallization and Hot Workability of 316LN Stainless Steel
Chaoyang Sun 1,*, Yu Xiang 1, Qingjun Zhou 2, Denis J. Politis 3, Zhihui Sun 1,* and Mengqi Wang 1 1 School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China; [email protected] (Y.X.); [email protected] (M.W.) 2 Capital Aerospace Machinery Company, Beijing 100076, China; [email protected] 3 Department of Mechanical Engineering, Imperial Co...
متن کاملdynamic recrystallization under hot deformation of a ph stainless steel
dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Manufacturing
سال: 2020
ISSN: 2351-9789
DOI: 10.1016/j.promfg.2020.08.067