Dynamic Fracture-Initiation Toughness ermination of Al 7075-T651 Aluminum Alloy

Application of the GTN Model in Ductile Fracture Prediction of 7075-T651 Aluminum Alloy

In this paper the capability of Gurson-Tvergaard-Needleman (GTN) model in the prediction of ductile damage in 7075-T651 aluminum alloy is investigated. For this purpose, three types of specimens were tested: Standard tensile bars, Round notched bar (RNB) specimens and compact tension (C(T)) specimens. Standard tensile bar tests were used to obtain the mechanical properties of the material and t...

evaluation of fatigue life of friction stir welded 7075-t651 aluminum alloy joints

abstract – aluminium 7075- t651 alloys are widely used in the production of light weight structures requiring a high strength to weight ratio and high corrosion resistance. the effect of processing parameters on fatigue life of 7075- t651 aluminium joints produced by friction stir welding was investigated in the present study. welding samples were made by employing rotating tool speed of 770, 9...

CORROSION BEHAVIOUR OF Al-Li-Cu-Mg ALLOY 8090-T651

Dynamic Shear Behaviour of Unweldable Aluminum-Scandium (Al-Sc) Alloy

This study uses a torsional split-Hopkinson bar to investigate the shear response and fracture characteristics of unweldable Al-Sc alloy during mechanical testing at shear strain rates of 800 s , 1500 s , 2200 s 1 and 2800 s 1 and temperatures of 150 C, 25 C and 300 C. The experimental results show that both the shear strain rate and the temperature have a significant effect on the shear proper...

Effect of loading rate on the plane stress fracture toughness properties of an aluminum alloy

The effect of loading rate on the plane stress fracture toughness properties of a 3.2-mm thick 2219-T87 aluminum alloy plate was investigated with center-cracked panels. Plane-stress J-resistance curves were generated at a constant displacement rate of 10-6 and 5.7 m s-l. Dynamic fracture testing was performed with a coupled pressure plates technique. Fracture initiation and propagation toughne...