Durability of Indium Tin Oxide-Silver-Indium Tin Oxide Films against Moisture Investigated Through The Wettability of The Top Oxide Layer
نویسندگان
چکیده
منابع مشابه
Enhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملFunctionalization of indium tin oxide.
The preparation and functionalization of ITO surfaces has been studied using primarily X-ray photoemission spectroscopy and infrared reflection-absorption spectroscopy (IRRAS) and the reagents n-hexylamine and n-octyltrimethoxysilane (OTMS). Particular attention has been paid to characterization of the surfaces both before and after functionalization. Surfaces cleaned by ultraviolet (UV)/ozone ...
متن کاملIndium Tin Oxide@Carbon Core–Shell Nanowire and Jagged Indium Tin Oxide Nanowire
This paper reports two new indium tin oxide (ITO)-based nanostructures, namely ITO@carbon core-shell nanowire and jagged ITO nanowire. The ITO@carbon core-shell nanowires (~50 nm in diameter, 1-5 μm in length,) were prepared by a chemical vapor deposition process from commercial ITO nanoparticles. A carbon overlayer (~5-10 in thickness) was observed around ITO nanowire core, which was in situ f...
متن کاملOrganosilane-functionalization of nanostructured indium tin oxide films.
Fabrication and organosilane-functionalization and characterization of nanostructured ITO electrodes are reported. Nanostructured ITO electrodes were obtained by electron beam evaporation, and a subsequent annealing treatment was selectively performed to modify their crystalline state. An increase in geometrical surface area in comparison with thin-film electrodes area was observed by atomic fo...
متن کاملCharacterization of Indium Tin Oxide Films after Annealing in Vacuum
ITO thin films were deposited on glass substrate by dc magnetron sputtering without substrate heating. The effects of annealing in vacuum on the structural, optical and electrical properties were investigated. The samples of 120 nm ITO films were separately annealed at 200, 250, 300 and 350°C for 1 hour. The results showed that the increasing of the annealing temperatures improve the crystallin...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2007
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.mer2007038