Ductility-dip cracking in weld metal of Fe-36%Ni alloy (Report II) - Characteristics of low ductility by simulated hot ductility test.
نویسندگان
چکیده
منابع مشابه
Weld Metal Ductility: Reduction in Area
It follows from the Chapter 7 that, except for very short gauge lengths, percent elongation is mainly influenced by uniform elongation, and is thus dependent upon the strain-hardening capacity of the matrix. In contrast, reduction in area is more a measure of the deformation required to produce fracture, and its chief contribution arises from the necking process. The work of Groom (1971) illust...
متن کاملHot Ductility Loss in a Fe-Ni-Based Superalloy
High temperature tensile tests have been conducted on samples of a Fe-Ni based superalloy, Incoloy A-286, and significant ductility loss has been observed at 1220 °C. Titanium-rich, thin-film-like phase has been found on the inter-granular facets of fracture surfaces. It appears that sulfur content of Ti-rich phase was higher than that of the matrix. At 1220 °C, liquation of Ti-rich phases has ...
متن کاملDuctility of Confined Concrete
Are structural engineers designing concrete structures with greater capacity and safety than they realize? By exploring effects of confinement in order to incorporate them in usual design procedures of engineering consulting companies, concrete structures will possibly in the future be both stronger, thinner and have a greater ability to deform prior to failure – three properties that are highl...
متن کاملDuctility of Nanostructured Bainite
Nanostructured bainite is a novel ultra-high-strength steel-concept under intensive current research, in which the optimization of its mechanical properties can only come from a clear understanding of the parameters that control its ductility. This work reviews first the nature of this composite-like material as a product of heat treatment conditions. Subsequently, the premises of ductility beh...
متن کاملVariability of Poisson’s Ratio and Enhanced Ductility in Amorphous Metal**
Ductile bulk metallic glass of composition 53.0Zr–18.7Cu–12.0Ni–16.3Al (at%) is plastically deformed under uniaxial compression and observed in situ by synchrotron high-energy X-ray diffraction. The diffraction patterns reveal the induced atomic strain is orientation dependent. At the onset of plastic deformation, the atomic strain in the compression direction saturates to a close-nearest-neigh...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 1985
ISSN: 0288-4771
DOI: 10.2207/qjjws.3.539