Ductile Fracture Characterization for Medium Carbon Steel Using Continuum Damage Mechanics
نویسندگان
چکیده
منابع مشابه
Progressive Damage Analysis of Laminated Composites using Continuum Damage Mechanics
In this paper, progressive damage and global failure of composite laminates under quasi-static, monotonic loading are investigated using 3D continuum damage mechanics. For this purpose, a finite element program has been developed using an eight-node 2D layered element including layer-wise plate theory. Damage analysis of a single orthotropic layer under various uniform in-plane and transverse l...
متن کاملDamage Assessment using an Inverse Fracture Mechanics approach
This paper studies the application of an inverse methodology for problem solving in fracture mechanics using the finite element analysis. The method was applied to both detection of subsurface cracks and the study of propagating cracks. The procedure for detection of subsurface cracks uses a first order optimization analysis coupled with a penalty function to solve for the unknown geometric par...
متن کاملMicromechanical characterization of ductile damage in DP steel
Weight minimization triggered the automotive industry to introduce new advanced high strength steels that show ductile fracture by microvoid evolution under deformation, resulting in unexpected failure without significant necking. Therefore, an extensive study was initiated to gain insight on the formation and development of microstructural damage in dual phase (DP) steel from a mechanical poin...
متن کاملEffect of Constraint on Ductile Crack Growth and Ductile-Brittle Fracture Transition of a carbon Steel
Ductile-brittle fracture transition was investigated using compact tension (CT) specimens from -70 o C to 40 o C for a carbon steel. Large deformation finite element analysis has been carried out to simulate the stable crack growth in the compact tension (CT, a/W=0.6), three point-point bend (SE(B), a/W=0.1) and centre-cracked tension (M(T), a/W=0.5) specimens. Experimental crack tip opening di...
متن کاملContinuum models of ductile fracture : A review
The past 20 years have seen substantial work on the modeling of ductile damage and fracture. Several factors explain this interest. (i) There is a growing demand to provide tools which allow to increase the efficiency of structures (reduce weight, increase service temperature or load, etc.) while keeping or increasing safety. This goal is indeed first achieved by using better materials but also...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Sciences and Applications
سال: 2012
ISSN: 2153-117X,2153-1188
DOI: 10.4236/msa.2012.311109