Does surface treatment with primers increase the shear bond strength between metallic bracket and monolithic zirconia?
نویسندگان
چکیده
Background: This was aimed to investigate the effect of surface treatment with different primers on shear bond strength (SBS) between metallic brackets and monolithic zirconia crowns.Methods: Sixty-five molar crowns were fabricated CAD-CAM technology. All underwent thermal cycling. After aging, randomly divided into five groups (n = 13) according cementation procedures: orthodontic bonding system; primer/composite paste: Transbond XT (TXT) (control); Group M: Monobond Plus (MP) applied surfaces then TXT composite paste; MT: MP crown paste TXT; Z: Z-Prime (ZP) ZT: ZP used for brackets. The bracket-bonded tested SBS using a universal testing machine. Results analyzed analysis variance.Results: A statistically significant difference found all regarding values (p=0.001). MT showed highest value, control group lowest value (p<0.05).Conclusion: It can be concluded that sufficient withstand forces. Surface contributes increase bracket zirconia.
منابع مشابه
Shear bond strength of indirect composite material to monolithic zirconia
PURPOSE This study aimed to evaluate the effect of surface treatments on bond strength of indirect composite material (Tescera Indirect Composite System) to monolithic zirconia (inCoris TZI). MATERIALS AND METHODS Partially stabilized monolithic zirconia blocks were cut into with 2.0 mm thickness. Sintered zirconia specimens were divided into different surface treatment groups: no treatment (...
متن کاملEffects of silanation time on shear bond strength between a gold alloy surface and metal bracket
OBJECTIVE We aimed to investigate the effects of silanation time on the shear bond strength (SBS) of metal brackets on gold alloy in a silicoating procedure and compare the SBS of metal brackets on gold alloy and enamel. METHODS Type III gold alloy plates were sandblasted with 30-µm silicon dioxide. Excess particles were removed with gentle air after silica coating, and silane was applied. Ma...
متن کاملShear bond strength of the repair composite resin to zirconia ceramic by different surface treatment.
INTRODUCTION The purpose of this study is the evaluation of the amount of surface roughness (Ra) of Zirconia Ceramic following different surface treatments as well as the assessment of its shear bond strength to composite resin. METHODS 40 sintered zirconia ceramic block samples were randomly divided in 4 groups of 10 and underwent the following surface treatments: a) Control group without tr...
متن کاملInfluence of surface modification techniques on shear bond strength between different zirconia cores and veneering ceramics
PURPOSE Veneering porcelain might be delaminated from underlying zirconia-based ceramics. The aim of this study was the evaluation of the effect of different surface treatments and type of zirconia (white or colored) on shear bond strength (SBS) of zirconia core and its veneering porcelain. MATERIALS AND METHODS Eighty zirconia disks (40 white and 40 colored; 10 mm in diameter and 4 mm thick)...
متن کاملShear Bond Strength of Metal brackets to Zirconia Treated with Er:YAG Laser Sandblasting and Silane
Background and Aim: Application of zirconia ceramics has increased. Since the commonly used surface treatment for porcelain, i.e. acid etching is not efficient for zirconia surfaces, evaluation of other surface treatment methods for zirconia is important. The aim of this study was to compare the shear bond strength (SBS) of metal brackets to zirconia treated with different powers of Er:YAG lase...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Selcuk dental journal
سال: 2022
ISSN: ['2148-7529']
DOI: https://doi.org/10.15311/selcukdentj.1128209