Do CVD grown graphene films have antibacterial activity on metallic substrates?
نویسندگان
چکیده
منابع مشابه
Transfer of CVD-grown monolayer graphene onto arbitrary substrates.
Reproducible dry and wet transfer techniques were developed to improve the transfer of large-area monolayer graphene grown on copper foils by chemical vapor deposition (CVD). The techniques reported here allow transfer onto three different classes of substrates: substrates covered with shallow depressions, perforated substrates, and flat substrates. A novel dry transfer technique was used to ma...
متن کاملNanoelectronic biosensors based on CVD grown graphene.
Graphene, a single-atom-thick and two-dimensional carbon material, has attracted great attention recently. Because of its unique electrical, physical, and optical properties, graphene has great potential to be a novel alternative to carbon nanotubes in biosensing. We demonstrate the use of large-sized CVD grown graphene films configured as field-effect transistors for real-time biomolecular sen...
متن کاملTransport Studies on CVD - Grown Graphene
In this thesis, we report transport studies performed on CVD-grown graphene. We perform resistivity and hall measurements on a large-area sample at 4' K. We measure the carrier mobility of the sample and find it to be on the order of 1000 cm 2/Vs, whereas monolayer graphene regularly exhibits much higher mobilities. We also examine what we find to be weak signatures of Shubnikov-de Haas oscilla...
متن کاملElectrical characterization of CVD diamond thin films grown on silicon substrates
Diamond thin films grown on high resistivity, (100) oriented silicon substrates by the hot filament chemical vapor deposition (HFCVD) method have been characterized by four-point probe and current-voltage (through film) techniques. The resistivities of the as-grown, chemically etched and annealed samples lie in the range of 1 O* fl cm to 10’ 0 cm. The Raman measurements on these samples indicat...
متن کاملPVD-grown antibacterial Ag-TiN films on piezoelectric PVDF substrates for sensor applications
This work reports on Ti1-xAgx and Ag-TiNx electrodes deposited by dc/pulsed dc magnetron sputtering at room temperature on poly (vinylidene fluoride) (PVDF) with the purpose to develop sensors for prosthesis. In Ti1-xAgx electrodes, silver content was varied from 0-100 at. %; and for Ag-TiNx electrodes, the nitrogen content was varied between 34 to 43 at. % and the Ti/Ag ratio changed from 12.2...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Carbon
سال: 2015
ISSN: 0008-6223
DOI: 10.1016/j.carbon.2014.12.025