Disassembly Study of Ultrasonically Welded Thermoplastic Composite Joints via Resistance Heating
نویسندگان
چکیده
منابع مشابه
An Experimental Study on the Tensile Behaviors of Ultrasonic Welded T-joints for Polyamide Composite
In this paper, an experimental investigation on ultrasonic welding of polyamide composites reinforced with glass fiber has been carried out. The effect of ultrasonic welding parameters, such as welding time, air pressure, hold time and the amount of glass fiber in the composite on tensile strength of weld joints were determined using response surface methodology. This methodology was applied fo...
متن کاملRelaxation behavior of polyethylene welded joints
The paper presents results of the investigation of structure relaxation and thermal properties of PE-80 and PE-100 polyethylene hot-tool butt welds. It was found that a weld with the re-crystallized crystalline structure is formed during the welding of dissimilar types of polyethylene. It is shown that within a long period (1 year) the relaxation occurs not only in amorphous but also in the cry...
متن کاملFatigue Life of Repaired Welded Tubular Joints
In this study, the effect of repair on fatigue life of tubular joints is investigated. Six cracked specimens precedently subjected to fatigue loading undergone to weld repair. Two of those specimens were shot peened before primary fatigue loading. It is shown that repair gives rise to about 150% increase in fatigue life for original specimens while the increase of fatigue life for shot-peened ...
متن کاملDisassembly Properties of Cementitious Finish Joints Using an Induction Heating Method
Efficient maintenance and upgrading of a building during its lifecycle are difficult because a cementitious finish uses materials and parts with low disassembly properties. Additionally, the reuse and recycling processes during building demolition also present numerous problems from the perspective of environmental technology. In this study, an induction heating (IH) method was used to disassem...
متن کاملFatigue Behaviour Study of Laser Hybrid Welded Eccentric Fillet Joints – Part Ii: State-of-the-art of Fracture Mechanics and Fatigue Analysis of Welded Joints
Simplified fatigue and fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineering components under normal and abnormal service loads. In many cases, welded joints are the regions most likely to contain original fabricatio...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials
سال: 2021
ISSN: 1996-1944
DOI: 10.3390/ma14102521