Direct chemical synthesis of L1(0)-FePtAu nanoparticles with high coercivity.
We report a facile synthesis of hard magnetic L10-FePtAu nanoparticles by coreduction of Fe(acac)3, Pt(acac)2 (acac = acetylacetonate) and gold acetate in oleylamine. In the current reaction condition, NP sizes are controlled to be 5.5 to 11.0 nm by changing the amount of Au doping. When the Au composition in the NPs is higher than 14%, the hard magnetic NPs are directly obtained without any an...
متن کاملPatterning of L10 FePt nanoparticles with ultra-high coercivity for bit-patterned media.
L10-ordered FePt nanoparticles (NPs) with ultra-high coercivity were directly prepared from a new metallopolyyne using a one-step pyrolysis method. The chemical ordering, morphology and magnetic properties of the as-synthesized FePt NPs have been studied. Magnetic measurements show the coercivity of these FePt NPs is as high as 3.6 T. Comparison of NPs synthesized under the Ar and Ar/H2 atmosph...
متن کاملSize-Dependent Chemical and Magnetic Ordering in L10-FePt Nanoparticles
FePt nanoparticles have great application potential in advanced magnetic materials such as ultrahigh-density recording media and high-performance permanent magnets. The key for applications is the very high uniaxial magnetocrystalline anisotropy of the L10-FePt phase, which is based on crystalline ordering of the face-centered tetragonal (fct) structure, described by the chemical-ordering param...
متن کاملSynthesis of Ultrafine SrFe12O19 Particles with High Coercivity
Ultrafine particles of SrFelzOts have been synthesized by citrate precursor technique. Solid state reactivity studies of citrate precursor lead to the formation oEfine particles of SrFe12019below 823K.Th.e size and m o r p h o l o g y o c e area measured by BETmethod for5.2nm clystallite is found to be27.45 m2fg. havingparticlesize42nm. UltrafinepaniclesofSrFe~zOlpshows interesting magnetic pro...
متن کاملChemical synthesis of low-coercivity, silica/Co composites for high-frequency magnetic components
The paper reports correlation between processing, structural and magnetic properties of cobalt nanoparticles dispersed in an insulating oxide matrix. High-temperature, chemical decomposition approach was utilized to achieve highly-dispersed, ultra-fine cobalt nanoparticles in silica matrix. Synthesis parameters such as precursor to passivating agent ratio were designed to control the metal-to-o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanoscale
سال: 2014
ISSN: 2040-3364,2040-3372
DOI: 10.1039/c4nr02345e