Dielectric study of calcium doped barium titanate Ba1-xCaxTiO3 ceramics
نویسندگان
چکیده
منابع مشابه
Synthesis of Barium-zinc-titanate Ceramics
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 °C for 2h with a heating rate of 10 °C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the pha...
متن کاملEffect of re-oxidation firing on PTCR properties of Sm-doped barium titanate ceramics
The effect of reduction and re-oxidation firing on the PTCR properties of Sm-doped barium titanate ceramics was investigated for the application in multilayered PTC thermistors. The lattice parameters a, and c decreases monotonically with increasing oxygen concentration in the re-oxidation atmosphere, which seems to be related with an electrostatic Coulomb interaction between an oxygen vacancy ...
متن کاملDielectric properties of binary polyvinylidene fluoride/barium titanate nanocomposites and their nanographite doped hybrids
Binary polyvinylidene fluoride/barium titanate(PVDF/BaTiO3) and its nanographite (GN) doped ternarynanocomposites were fabricated using a simple solution casting process followed by compression molding. The dielectricbehavior of such hybrids over a wide frequency range was studied. Additions of GN with contents close to the percolationthreshold were found to be very effective to...
متن کاملH all effect and dielectric properties of Mn - doped barium titanate
BaMn Ti O (0# x # 0.01) ceramics have been prepared using a sol–gel method. The Hall coefficient, x 12x 3 leakage conductance and dielectric constant were measured. The Hall effect confirms that the charge carriers of the ceramics are electrons, and the electronic concentration n 5 1/ ueRu decreases with increasing Mn 31 41 concentration. We propose that Mn and Mn substitution of Ti can partial...
متن کاملDc and Ac Electrical Properties of Ptc Barium Titanate Ceramics
The dc and ac electrical properties of PTC barium titanate ceramics were measured in the temperature range from 30 to 450°C. The Heywang's model alone is not sufficient to perform a quantitative analysis of the results. The heterogeneity of the system is taken into account.
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Physical Sciences
سال: 2016
ISSN: 1992-1950
DOI: 10.5897/ijps2015.4415