Dielectric Properties in LiTaO3-CaTiO3 Solid Solution Ceramics

Core-shell Grain Structures and Dielectric Properties of Na0.5K0.5NbO3-LiTaO3-BiScO3 Piezoelectric Ceramics

The origins of distinctive compositional dependence of relative permittivity, 計r, in the Pb-free piezoelectric system (1-x)Na0.5K0.5NbO3-xLiTaO3, x≤ 10 mol% modified with BiScO3 have been revealed using transmission electron microscopy with energy dispersive X-ray analysis (TEM-EDX). As the LiTaO3 content increased the Curie peak at ~370°C in 計r –T plots became more diffuse, and at x= 5 mol% an...

LOW-TEMPERATURE SINTERING AND MICROWAVE DIELECTRIC PROPERTIES OF (Zn0.65Mg0.35)TiO3-CaTiO3 CERAMICS WITH H3BO3 ADDITION

Low-melting H3BO3, acting as sintering aid, was used to reduce the sintering temperature of 5 wt.% CaTiO3-doped (Zn0.65Mg0.35)TiO3 ceramics. The sintering behaviors, microstructures and microwave dielectric properties with different amounts of H3BO3 addition were investigated. The results showed that H3BO3 additive was very effective for lowering the sintering temperature and improving the bulk...

Crystal Structure, Infrared Spectra and Microwave Dielectric Properties of Temperature Stable Zircon-Type (Y,Bi)VO4 Solid Solution Ceramics

THE COMPARISON OF MECHANICAL PROPERTIES OF SINTERED ?. QUARTZ SOLID SOLUTION AND GAHNITE GLASS – CERAMICS IN ZNO-AL2O3-SIO2 SYSTEM

The effect of precipitation of ?.qss. and gahnite phases during heat treatment of glass frits in the ZnO-Al2O3-SiO2 system on the mechanical property of resulting glass-ceramic specimens were investigated. It was shown that gahnite glass-ceramics had higher bend strength and toughness values than ?.qss. ones. The results are attributed to the higher modulus of elasticity as well as higher therm...

Core–shell grain structures and ferroelectric properties of Na0.5K0.5NbO3–LiTaO3–BiScO3 piezoelectric ceramics

Legislation arising from health and environmental concerns has intensified research into finding suitable alternatives to lead-based piezoceramics. Recently, solid solutions based on sodium potassium niobate (K,Na)NbO3 (KNN) have become one of the globally-important lead-free counterparts, due to their favourable dielectric and piezoelectric properties. This data article provides information on...