Diabase Mud-Based Geopolymer Paste: Formulation and Properties
نویسندگان
چکیده
The concepts of sustainability and waste utilization have received urgent attention in the European construction industries. Material selection plays a vital role manufacturing process sustainable building construction. general objective this study is transformation diabase mud into value-added product. was characterized, different parameters were selected for cement, as well metakaolin mixture. This paper includes analytical research results geopolymer paste embedded with material its precursor, combination sodium hydroxide (NaOH) silicate (Na2SiO3) alkaline activators to form geopolymeric system. compressive strength optimum mix sample recorded 14.0 MPa at 72 h. embedding resulted viable composite use industry.
منابع مشابه
Mechanical Properties and Microstructure of Class C Fly Ash-Based Geopolymer Paste and Mortar
This paper presents workability, compressive strength and microstructure for geopolymer pastes and mortars made of class C fly ash at mass ratios of water-to-fly ash from 0.30 to 0.35. Fluidity was in the range of 145-173 mm for pastes and 131-136 mm for mortars. The highest strengths of paste and mortar were 58 MPa and 85 MPa when they were cured at 70 °C for 24 h. In XRD patterns, unreacted q...
متن کاملPreparation and Properties of Alkali Activated Metakaolin-Based Geopolymer
The effective activation and utilization of metakaolin as an alkali activated geopolymer precursor and its use in concrete surface protection is of great interest. In this paper, the formula of alkali activated metakaolin-based geopolymers was studied using an orthogonal experimental design. It was found that the optimal geopolymer was prepared with metakaolin, sodium hydroxide, sodium silicate...
متن کاملOptimization of NaOH Molarity, LUSI Mud/Alkaline Activator, and Na2SiO3/NaOH Ratio to Produce Lightweight Aggregate-Based Geopolymer
This paper presents the mechanical function and characterization of an artificial lightweight geopolymer aggregate (ALGA) using LUSI (Sidoarjo mud) and alkaline activator as source materials. LUSI stands for LU-Lumpur and SI-Sidoarjo, meaning mud from Sidoarjo which erupted near the Banjarpanji-1 exploration well in Sidoarjo, East Java, Indonesia on 27 May 2006. The effect of NaOH molarity, LUS...
متن کاملInvestigation of Mechanical Properties of Lithium-Based Geopolymer Composites Reinforced with Basalt Fibers
Recently, geopolymer binders have been considered because of low cost, simple processes for synthesis and many raw materials in nature. Geopolymer with brittle nature does not have high strength and cannot be used alone for structural materials. Therefore, to use in different structures, the composite which is reinforced with fibers such as carbon, glass, basalt, etchasbeen used. In this resear...
متن کاملTaftan Pozzolan-Based Geopolymer Cement
Abstract: In recent years, many research works have been done to investigate the possibility of utilizing a broad range of materials as raw materials in the production of geopolymer cements. The use of artificial pozzolans or aluminosilicate-type industrial waste materials such as granulated blast-furnace slag and fly ash has been reported in many research works. Natural pozzolans are also al...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials proceedings
سال: 2021
ISSN: ['2673-4605']
DOI: https://doi.org/10.3390/materproc2021005077