Development of Zn-Ni alloy plated steel sheet.
نویسندگان
چکیده
منابع مشابه
Corrosion Protection of Steel Using Nonanomalous Ni-Zn-P Coatings
A novel technique for obtaining nonanomalous Ni-Zn-P coatings with high Ni content ~74 wt % as compared to 15-20 wt % in the conventional plating method! has been developed. These coatings show promise as a replacement for Cd in sacrificially protecting steel. Ni-Zn-P coatings were deposited using an electroless method from a solution containing NiSO4 , complexing agent and ammonium chloride. V...
متن کاملINVESTIGATION OF THE MECHANICAL, CORROSION PROPERTIES AND WEAR BEHAVIOUR OF ELECTROLESS Ni-P PLATED MILD STEEL
In the present study the mild steel (MS) specimens were coated with Nickel-Phosphorus (Ni-P) using acrylic bath. Heat treatment was carried out on specimens under different temperatures and time periods in an inert atmosphere. The various mechanical and tribological tests were performed on specimens. Using weight loss method, the corrosion nature of the samples under different environments was ...
متن کاملDevelopment of Corrosion Resistant Zn-Ni-TiO2 Composite Coatings
The Zn-Ni-TiO2 composite coatings were developed on mild steel by electrodeposition method. The bath constituents (ZnSO4.6H2O, NiSO4.6H2O, TiO2, thiamine hydrochloride) and operating conditions (temperature and pH) were optimized by Hull cell method, for peak performance of the coating against corrosion. The coatings were prepare...
متن کاملNumerical and Experimental Investigations on Springback of U-bending of DP600 Steel Alloy Sheet
The most prominent feature of sheet material forming process is an elastic recovery phenomenon during unloading which leads to springback and side wall curl. Therefore evaluation of springback and side wall curl is mandatory for production of precise products. In this paper, the effects of some parameters such as friction coefficient, sheet thickness, yield strength of sheet and blank-holder fo...
متن کاملElectroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys
a r t i c l e i n f o Zn–Ni, Zn–Co and Zn–Ni–Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Metal Finishing Society of Japan
سال: 1986
ISSN: 1884-3395,0026-0614
DOI: 10.4139/sfj1950.37.55