Enhancement of the Magnetic Properties for Co-Mn-Zn Ferrites
Aluminum substituted cobalt manganese zinc ferrite nanoparticles Co0.425Mn0.425Zn0.150AlxFe2-xO4 (from x= 0.0 to 0.15 with step 0.025) have been synthesized by chemical co-precipitation route. X-ray diffraction (XRD) and infrared spectroscopy (FTIR) revealed that the obtained powders have a single phase of cubic spinel structure. The crystallite sizes calculated from XRD data have been confirme...
متن کاملEnhancement of Néel temperature and electrical resistivity of Mn–Ni–Zn ferrites by Gd3+ substitution
Structural, magnetic, and dielectric properties of various Mn0.5Ni0.1Zn0.4Fe2−xGdxO4 sintered at 1200 ◦C were investigated thoroughly. The samples were synthesized by standard solid state reaction technique. The crystal structure was characterized by X-ray diffraction (XRD), which has confirmed the formation of single phase spinel structure. Bulk density, average grain size and initial permeabi...
متن کاملInfluence of B2O3 on the Production of Pure, Gel-Processed Mn-Zn Ferrites
The influence of B203 on the microshucture and magnetic properties of pure Mn-Zn ferrites has been investigated. A citrate gel processing route was employed to produce highly homogeneous Mn-Zn (MQ,~,Z~.,F~,,OJ ferrites undoped or doped with B203 (0-2.5wt%). The results show that B203 doping does not benefit the magnetic properties of these femtes, but promoted grain growth significantly. The in...
متن کاملElectrical and magnetic properties of Mn-Ni-Zn ferrites processed by citrate precursor method
MnxNi0.5 _ xZn0.5Fe2O4, (x = 0.05, 0.1, 0.2, 0.3, 0.4) ferrites synthesized by the citrate precursor method are investigated in the present work. Compositional variation of AC resistivity is studied and values up to 10 times greater than those for samples prepared by the conventional ceramic method are observed. It is found that resistivity decreases with increase in Mn concentration except for...
متن کاملThe Manufacture of High Permeability Mn-Zn Ferrites by Atmospherical Protect
For the manufacture of high permeability Mn-Zn ferrite cores, the zinc loss from the surface of sintering cores causes poor yield rate of final products. This experiment uses the atmospherical protection to reduce the evaporation of zinc. The control of the oxygen partial pressure and flow rate precisely can reduce the zinc loss about 20% to 35%, but it is not enough to get a good distribution ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1996
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.43.1386