Development of fatigue cracks from mechanically machined scratches on 2024-T351 aluminium alloy-Part II: finite element analysis and prediction method

نویسندگان
چکیده

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Fatigue of Friction Stir Welded 2024-T351 Aluminium Alloy

Fatigue failure characteristics of friction stir welds in 13mm gauge 2024-T351 plate have been assessed. Failure occurred from either the weld region (nugget/flow arm) or from the material immediately surrounding the weld. Fatigue failure from the surrounding material was essentially conventional, initiating from large S-phase intermetallic particles and growing in a macroscopic mode I manner. ...

متن کامل

Effect of Tool Profile and Fatigue Loading on the Local Hardness Around Scratches in Clad and Unclad Aluminium Alloy 2024

Nanoindentation has been used to study the hardness changes produced by scratching of aluminium alloy AA2024, with and without a clad layer of pure aluminium. The hardness was mapped around scratches made with diamond tools of different profiles. One tool produced significant plastic damage with associated hardening at the scratch root, whilst the other produced a ‘cleaner’ cut with no hardenin...

متن کامل

A Theoretical and Practical Study of Cracking of an Aluminium Alloy During Side Pressing Using a Finite - Element Analysis

Elastic-plastic finite-element analysis applied to metalforming allows the real macroscopic properties of the workpiece to be incorporated. This paper presents the results of an experimental study of the initiation of cracking in side-pressing of a heat-treated aluminium alloy (Duralloy 2014). Using an F. E. analysis, these are related to various fracture criteria. It is found that the criterio...

متن کامل

Fatigue and Anisotropic behaviours of cold rolled AA1200 Aluminium Alloy

This study examines the fatigue and anisotropy behaviour of cold rolled AA1200 aluminium alloy for light weight automotive connecting rod application. Aluminium (Al) 1200 ingots were melted at temperature of 680 0C (after one hour of heating) cast in sand mould and cast samples homogenized for 6 hrs at 480 0C. The cold rolling process was carried out after homogenisation for 10, 20, 30, 40 and ...

متن کامل

Fatigue crack propagation of multiple coplanar cracks with the coupled extended finite element/fast marching method

A numerical technique for modeling fatigue crack propagation of multiple coplanar cracks is presented. The proposed method couples the extended finite element method (X-FEM) [Int. J. Numer. Meth. Engng. 48 (11) (2000) 1549] to the fast marching method (FMM) [Level Set Methods & Fast Marching Methods: Evolving Interfaces in Computational Geometry, Fluid Mechanics, Computer Vision, and Materials ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Fatigue & Fracture of Engineering Materials & Structures

سال: 2016

ISSN: 8756-758X

DOI: 10.1111/ffe.12545