Development & characterization of alumina coating by atmospheric plasma spraying
نویسندگان
چکیده
منابع مشابه
Plasma spraying and characterization of chromium carbide – nickel chromium coatings
Chromium carbide – nickel chromium powder Cr3C2-25wt.NiCr was plasma sprayed by a water-stabilized system WSP®. A series of experiments with variable feeding distance was carried out. Basic characterization of coatings was done by XRD, SEM and light microscopy plus image analysis. Microhardness was measured on polished cross sections. The main focus of investigation was on resistances against w...
متن کاملDirect current plasma spraying of mechanofused alumina - steel particles
Stainless steel particles (60 μm in mean diameter) cladded with an alumina shell (2 μm thick and manufactured by mechanofusion) were sprayed with an Ar-H2 (53-7 slm) d.c. plasma jet (I = 500 A, P = 28 kW, th = 56 %). Two main types of particles were collected in flight, as close as 50 mm downstream of the nozzle exit: particles with a steel core with pieces of alumina unevenly distributed at t...
متن کاملMicrostructure and Property of Zr-Based Metallic Glass Coating Formed by Gas Tunnel Type Plasma Spraying
Metallic glass has excellent functions such as high strength and high corrosion resistance. Therefore, it is one of the most attractive materials, and various developmental research works have been conducted by many researchers. However, the metallic glass material is expensive to use, and a composite material is preferred for the industrial application. Thermal spraying method is one of potent...
متن کاملSplat Formation and Nanohardness Investigation of Atmospheric Plasma Sprayed Alumina
Atmospheric plasma spraying (APS) is a well established process for preparing ceramic coatings. In this process, powder particles injected into the plasma jet are heated and accelerated simultaneously in the plasma stream and are deposited in molten or semi-molten droplets conditions onto a prepared substrate. During droplet impingement, these molten droplets rapidly solidify to form single spl...
متن کاملProperties-Adjustable Alumina-Zirconia Nanolaminate Dielectric Fabricated by Spin-Coating
In this paper, an alumina-zirconia (Al₂O₃-ZrO₂) nanolaminate dielectric was fabricated by spin-coating and the performance was investigated. It was found that the properties of the dielectric can be adjusted by changing the content of Al₂O₃/ZrO₂ in nanolaminates: when the content of Al₂O₃ was higher than 50%, the properties of nanolaminates, such as the optical energy gap, dielectric strength (...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2018
ISSN: 1757-8981,1757-899X
DOI: 10.1088/1757-899x/330/1/012043