Development and characterization of nickel-zinc spinel ferrite for microwave absorption at 2·4 GHz
نویسندگان
چکیده
منابع مشابه
Synthesis and Characterization of Nickel Zinc Ferrite Nanoparticles
In this research nickel zinc ferrite nanoparticles with composition of Ni1-xZnxFe2O4 (where x=0, 0.3, 0.7, 1) were synthesized by a sol-gel method at 600 °C for 5 hours. The structure of nanoparticles was studied using X-ray diffraction pattern. The lattice parameter of ferrite nanoparticles was calculated and indicates lattice constant of nanoparticl...
متن کاملSynthesis and characterization of nanocrystalline spinel Zinc ferrite prepared by sol-gel auto-combustion technique
Sol–gel auto-combustion is a unique combination of the combustion and the chemical gelation processes. In this work, nanosize (d) powders with compositions of ZnFe2O4 were synthesized by sol–gel combustion method. The puffy, porous brown powders as-combusted was calcined at the temperature of 750–1000◦C for 4 h. These powders are characterized by X-ray diffraction and scanning electron microsco...
متن کاملSynthesis and characterization of nanocrystalline spinel Zinc ferrite prepared by sol-gel auto-combustion technique
Sol–gel auto-combustion is a unique combination of the combustion and the chemical gelation processes. In this work, nanosize (d) powders with compositions of ZnFe2O4 were synthesized by sol–gel combustion method. The puffy, porous brown powders as-combusted was calcined at the temperature of 750–1000◦C for 4 h. These powders are characterized by X-ray diffraction and scanning electron microsco...
متن کاملsynthesis and characterization of nickel zinc ferrite nanoparticles
in this research nickel zinc ferrite nanoparticles with composition of ni1-xznxfe2o4 (where x=0, 0.3, 0.7, 1) were synthesized by a sol-gel method at 600 °c for 5 hours. the structure of nanoparticles was studied using x-ray diffraction pattern. the lattice parameter of ferrite nanoparticles was calculated and indicates lattice constant of nanoparticles depend on zinc concentration. the crystal...
متن کاملCorrection: Growth and crystallographic feature-dependent characterization of spinel zinc ferrite thin films by RF sputtering
Correction Figure 4g in the original version of this article [1] was misused in the typesetting process. The figure 4g is the same as figure 4a. The corrected image for figure 4g is shown here (Figure 1). Reference 1. Liang YC, Hsia HY: Growth and crystallographic feature-dependent characterization of spinel zinc ferrite thin films by RF sputtering. Figure 1 Low-magnification TEM image of the Z...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Bulletin of Materials Science
سال: 2008
ISSN: 0250-4707,0973-7669
DOI: 10.1007/s12034-008-0121-2