Deuterium retention in MeV self-implanted tungsten: Influence of damaging dose rate
نویسندگان
چکیده
منابع مشابه
Implantation Energy Dependence on Deuterium Retention Behaviors for the Carbon Implanted Tungsten
Yasuhisa Oya*, Makoto Kobayashi, Naoaki Yoshida, Naoko Ashikawa, Akio Sagara, Yuji Hatano, and Kenji Okuno 1) Radioscience Research Laboratory, Faculty of Science, Shizuoka University, 836, Ohya, Suruga-ku, Shizuoka 422-8529, Japan. 2) Institute for Applied Mechanics, Kyushu University, Fukuoka 816-8580, Japan. 3) National Institute for Fusion Science, Gifu 509-5292, Japan. 4) Hydrogen Isotope ...
متن کاملImpact of beryllium surface layers on deuterium retention in tungsten
In ITER mixed Be/W layers are likely to form and their retention behavior is unknown. A series of ITER-grade tungsten samples have been exposed in PISCES-B to deuterium plasma at 300oC, with and without beryllium impurity seeding of the plasma. If the beryllium concentration is small, the majority of the incident beryllium is re-eroded from the sample surface and only a few nm thick layer of mi...
متن کاملDeuterium diffusion and retention in a tungsten-carbon multilayer system
A tungsten-carbon multilayer system deposited by magnetron sputtering was used as a model system to study deuterium diffusion in tungsten, carbon and related carbides. After deposition the as-deposited multilayer films were annealed at different temperatures to achieve different structures. The structural changes due to annealing were investigated by Rutherford backscattering spectrometry and X...
متن کاملAnnealing kinetics of vacancy-related defects in low-dose MeV self-ion-implanted n-type silicon
Silicon samples of n-type have been implanted at room temperature with 5.6-MeV Si ions to a dose of 2310 cm and then annealed at temperatures from 100 to 380 °C. Both isothermal and isochronal treatments were performed and the annealing kinetics of the prominent divacancy (V2) and vacancy-oxygen ~VO! centers were studied in detail using deep-level transient spectroscopy. The decrease of V2 cent...
متن کاملCorrelation between desorption of deuterium and recovery of irradiation defects in simultaneously deuterium and carbon ion-implanted tungsten
defects in simultaneously deuterium and carbon ion-implanted tungsten Rie KURATA, Makoto KOBAYASHI, Sachiko SUZUKI, Wanjing WANG, Naoko ASHIKAWA, Akio SAGARA, Naoaki YOSHIDA, Yasuhisa OYA, and Kenji OKUNO 1) Radioscience Research Laboratory, Faculty of Science, Shizuoka University, 836, Ohya, Suruga-ku, Shizuoka 422-8529, Japan 2) National Institute for Fusion Science, Japan 3) Institute of App...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nuclear Materials and Energy
سال: 2017
ISSN: 2352-1791
DOI: 10.1016/j.nme.2017.02.003