Desulphurization of Carbon-free Liquid Iron Contained in Lime Crucible with Aluminum
نویسندگان
چکیده
منابع مشابه
DIRECT REDUCTION OF SARCHESHME COPPER SULFIDE CONCENTRATE WITH CARBON IN THE PRESENCE OF LIME
Abstract: The direct reduction of copper sulfide concentrate from Iranian Sarcheshme deposits with carbon in the presence of lime was investigated in the temperature range of 800-1000 ºC. The reduction kinetics was determined by means of weight loss measurements. It was found that the rate of reaction increased considerably with increasing the temperature. The kinetics was also improved whe...
متن کاملBimetallic iron-aluminum particles for dechlorination of carbon tetrachloride.
Bimetallic iron-aluminum (Fe/Al) particles were synthesized and tested for their reactivity toward carbon tetrachloride using batch reactors and a flow-through column at near neutral pH. Preparation of bimetallic Fe/Al particles was conducted under acidic conditions under which iron was readily deposited onto the aluminum surface. The SEM image showed clusters of iron on the aluminum surface at...
متن کاملThe Research on Desulphurization of an Iron Concentrate
Iron ore concentrate sales in a mineral processing plant appeared a trend of high sulfur, exceeding the sales requirement of 0.3% significantly. To this end, for the sulfide in iron concentrate mainly exists in the form of pyrrhotite, companies with iron minerals and has a high degree of oxidation, we can add flotation agent to the magnetic separation column, and at the same time fill gas for s...
متن کاملEffect of Aluminum on Microstructure and Thickness of Galvanized Layers on Low Carbon silicon-Free Steel
In hot dip galvanizing, several parameters such as chemical composition of coating bath, immersion time and surface roughness of specimens could affect microstructure and properties of coating. In this article, the effect of aluminum content, immersion time and surface roughness on structure and properties of alloy layers have been investigated. Specimens of low carbon silicon-free steel with d...
متن کاملdetermination of maximal singularity free zones in the workspace of parallel manipulator
due to the limiting workspace of parallel manipulator and regarding to finding the trajectory planning of singularity free at workspace is difficult, so finding a best solution that can develop a technique to determine the singularity-free zones in the workspace of parallel manipulators is highly important. in this thesis a simple and new technique are presented to determine the maximal singula...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Iron and Steel Institute of Japan
سال: 1976
ISSN: 0021-1583,1881-1183
DOI: 10.2355/isijinternational1966.16.304