Dendrite growth simulation of Al-Zn alloys by the phase field method
نویسندگان
چکیده
منابع مشابه
Phase-field modeling of the dendrite orientation transition in Al-Zn alloys
With a few exceptions, phase-field simulations of dendritic growth in cubic materials have been modeled using simple expressions for the interfacial energy anisotropy and with strong anisotropy. However, recent experimental results show that the Dendrite Orientation Transition (DOT) observed in Al-Zn alloys by Gonzales and Rappaz [Met. Mat. Trans. A37 (2006) 2797] occurs at weak anisotropy, and...
متن کاملDendritic Growth Morphologies in Al-Zn Alloys—Part II: Phase-Field Computations
In Part I of this article, the role of the Zn content in the development of solidification microstructures in Al-Zn alloys was investigated experimentally using X-ray tomographic microscopy. The transition region between h100i dendrites found at low Zn content and h110i dendrites found at high Zn content was characterized by textured seaweed-type structures. This Dendrite Orientation Transition...
متن کاملMicrostructure of Al-Zn and Zn-Al Alloys*
The change of microstructure of the title alloys with concentration, temperature and applied thermal treatment was studied in situ by XRD. The alloys, having the Zn atomic fraction, x(Zn), from 0.03 to 0.62, were subjected to: (i) rapid quenching from a temperature, Tt, higher than the solid-solution temperature, Tss, in water at RT (samples WQ); (ii) slow cooling from Tt to RT (samples SC). Th...
متن کاملGrowth directions in directionally solidified Al–Zn and Zn–Al alloys near eutectic composition
Growth directions and crystallographic orientations of solidification microstructures have been measured in Al–Zn alloy near the eutectic composition. Al dendrites in Al–92 wt.% Zn alloy were found to grow along the h110i directions while Zn dendrites in Al– 96 and 98 wt.% Zn have h10 10i trunks. In the lamellar eutectic, a crystallographic relationship has been found between the dense plane of...
متن کاملTwinned dendrite growth in binary aluminum alloys
The formation of twinned dendrites (feathery grains) in binary Al–Zn, Al–Mg, Al–Cu and Al–Ni alloys has been studied in specimens directionally solidified under identical thermal conditions, i.e. G 100 K cm , v 1 mm s , and with slight natural convection in the melt. The influence of the solute element nature and content has been found to be of less importance than previously reported since fea...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 2005
ISSN: 0451-5994,1880-8018
DOI: 10.2464/jilm.55.2