Degradation of Multilayer Ceramic Capacitors with Nickel Electrodes under Highly Accelerated Life Test.
نویسندگان
چکیده
منابع مشابه
Highly Accelerated Life Stress Testing (HALST) of Base-Metal Electrode Multilayer Ceramic Capacitors
An improved highly accelerated life stress test (HALST) procedure and modeling method was developed to evaluate the reliability of multilayer ceramic capacitors with base-metal electrodes (BMEs). Reliabilities of ceramic capacitors with precious-metal electrodes (PMEs) and BMEs are discussed. A combination of leakage current and mean-time-to-failure (MTTF) measurements under accelerated life st...
متن کاملParasitic Inductance of Multilayer Ceramic Capacitors
The parasitic inductance of multilayer ceramic capacitors (MLCCs) is becoming more important in the decoupling of high speed digital systems. There exists conflicting data and statements on the parasitic inductance of the MLCC. This work shows the measurement techniques of the inductance parameters, focusing mainly on the fixturing needed to accurately measure the chips. The effects of various ...
متن کاملAccelerated Degradation Test and Predictive Failure Analysis of B10 Copper-Nickel Alloy under Marine Environmental Conditions
This paper studies the corrosion behavior of B10 copper-nickel alloy in marine environment. Accelerated degradation test under marine environmental conditions was designed and performed based on the accelerated testing principle and the corrosion degradation mechanism. With the prolongation of marine corrosion time, the thickness of Cu₂O film increased gradually. Its corrosion product was Cu₂(O...
متن کاملTitle of dissertation : MOISTURE IN MULTILAYER CERAMIC CAPACITORS
Title of dissertation: MOISTURE IN MULTILAYER CERAMIC CAPACITORS Daniel Noel Donahoe, Doctor of Philosophy, 2005 Dissertation directed by: Professor Michael G. Pecht Department of Mechanical Engineering When both precious metal electrode and base metal electrode (BME) capacitors were subjected to autoclave (120 oC/100 % RH) testing, it was found that the precious metal capacitors aged according...
متن کاملHumidity-bias Effects on Reliability of Multilayer Ceramic Capacitors
Title of dissertation: FLEX CRACKING AND TEMPERATUREHUMIDITY-BIAS EFFECTS ON RELIABILITY OF MULTILAYER CERAMIC CAPACITORS Mohammadreza Keimasi, Doctor of Philosophy, 2007 Dissertation directed by: Professor Michael Pecht Department of Mechanical Engineering Multilayer ceramic capacitors (MLCCs) are known to be susceptible to cracking when subjected to excessive printed circuit board (PCB) flexu...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1995
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.42.557