Degradation characteristics due to mechanical fatigue of epoxy micaceous insulations.
نویسندگان
چکیده
منابع مشابه
Optimalization of the Thermal Curing of Epoxy Based Insulations
There is difficult to imagine modern production of electrical devices without components containing organic substances. This fact is mainly concerned to composite materials, in which the bond component is made of organic substance. The intricate curing reactions have been proceeding during the composites technological curing as well as during the device operation, where mostly the thermal-oxida...
متن کاملMechanical Properties of Graphene/Epoxy Nanocomposites under Static and Flexural Fatigue Loadings
In the present study, the effect of various weight fractions of graphene nanoplatelet (GPL) on flexural fatigue behavior of epoxy polymer has been investigated at room temperature and generally the temperature was monitored on the surface of specimen during each test. The flexural stiffness of grapheme nano-platelet/epoxy nanocomposites at 0.1, 0.25 and 0.5 wt. % as a main effective parameter o...
متن کاملCharacterization of a fracture specimen for crack growth in epoxy due to thermal fatigue
Finite element simulations are carried out to characterize a new fracture specimen, consisting of an outer circular epoxy ring bonded to an inner circular invar plate for accelerated thermal fatigue testing. Radial cracks are introduced in the epoxy ring. The growth of these radial cracks is correlated to the applied energy release rate G. We studied the dependence of G on the crack length, the...
متن کاملFactors involved in mechanical fatigue degradation of dental resin composites.
The design of clinical trials allows for limited insights into the fatigue processes occurring in resin composites and the factors involved therein. In vitro studies, in contrast, can fundamentally narrow study interests to focus on particular degradation mechanisms and, to date, represent the major contributors to the state of knowledge on the subject. These studies show that microstructural f...
متن کاملmechanical properties of graphene/epoxy nanocomposites under static and flexural fatigue loadings
in the present study, the effect of various weight fractions of graphene nanoplatelet (gpl) on flexural fatigue behavior of epoxy polymer has been investigated at room temperature and generally the temperature was monitored on the surface of specimen during each test. the flexural stiffness of grapheme nano-platelet/epoxy nanocomposites at 0.1, 0.25 and 0.5 wt. % as a main effective parameter o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IEEJ Transactions on Fundamentals and Materials
سال: 1985
ISSN: 0385-4205,1347-5533
DOI: 10.1541/ieejfms1972.105.142