Deformation-texture evolution in deep drawing of cold-rolled 3104 aluminum alloy sheet
نویسندگان
چکیده
منابع مشابه
Statistical analysis on static recrystallization texture evolution in cold-rolled AZ31 magnesium alloy sheet.
Cast AZ31B-H24 magnesium alloy, comprising Mg with 3.27 wt% Al and 0.96 wt% Zn, was cold rolled and subsequently annealed. Global texture evolutions in the specimens were observed by X-ray diffractometry after the thermomechanical processing. Image-based microstructure and texture for the deformed, recrystallized, and grown grains were observed by electron backscattered diffractometry. Recrysta...
متن کاملPrediction of earing in deep drawing of anisotropic aluminum alloy sheet using BBC2003 yield criterion
This paper investigates the earing phenomenon in deep drawing of AA3105 aluminum alloy, experimentally and numerically. Earing defect is mainly attributed to the plastic anisotropy of sheet metal. In order to control such defect, predicting the evolution of ears in sheet metal forming analyses becomes indispensable. In this regard, the present study implements the advanced yield criterion BBC20...
متن کاملprediction of earing in deep drawing of anisotropic aluminum alloy sheet using bbc2003 yield criterion
this paper investigates the earing phenomenon in deep drawing of aa3105 aluminum alloy, experimentally and numerically. earing defect is mainly attributed to the plastic anisotropy of sheet metal. in order to control such defect, predicting the evolution of ears in sheet metal forming analyses becomes indispensable. in this regard, the present study implements the advanced yield criterion bbc20...
متن کاملThe Influence of Surface Roughness of Drawbead on Non-Symmetry Deep Drawing Cold Rolled Steel Sheet
This study was aimed to explain the influence of surface roughness of the drawbead on non-symmetry deep drawing cold rolled steel sheet to improve the drawability of cold rolled steel sheet. The variables used in this study included semi-circle drawbead with 3 levels of surface roughness which are 6.127 μm Ra, 0.963 μm Ra and 0.152 μm Ra and cold rolled steel sheet according to 3 grades of the ...
متن کاملMicrostructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 2019
ISSN: 0451-5994,1880-8018
DOI: 10.2464/jilm.69.387