Deformation mechanisms of hard oriented NiAl single crystals
نویسندگان
چکیده
منابع مشابه
High Temperature Internal Friction in NiAl Single Crystals
The internal friction of high-purity NiAl single crystals was investigated utilizing a low-frequency subresonance torsion a p m . Above lOOOK the damping increases strongly up to Q-' =0.3 at 1400K. The activation enthalpy of this viscoelastic relaxation depends on the composition and shows the highest value (2.8eV) for stoichiometric NiAl. The results are discussed in terms of diffusionantrolle...
متن کاملPseudoelastic Deformation of CuAlMn Single Crystals
Martensitic transformation associated with a tensile deformation of CuAlMn single crystals in [loo] direction was studied using in-situ transmission electron microscopy. Stress/strain curves obtained during pseudoelastic deformation of microscopic samples were slightly different fiom bulk ones due to martensite formation in the stage of stress increase and a permanent deformation during the fir...
متن کاملPlastic deformation of CoO single crystals
2014 Constant strain rate compressions along 001 > have been performed on CoO single crystals (03B5 ~ 6 x 10-5 s-1). Yield stresses and work hardening rates have been measured between 77 K and 1 400 K; CoO is very strong when compared to similar compounds. Vickers indentations have been performed on { 100 }, { 110 } and { 111 } faces around the Néel temperature, i.e. between 0 °C and 40 °C...
متن کاملPlastic deformation of single nanometer-sized crystals.
We report in situ electron microscopy observations of the plastic deformation of individual nanometer-sized Au, Pt, W, and Mo crystals. Specifically designed graphitic cages that contract under electron irradiation are used as nanoscopic deformation cells. The correlation with atomistic simulations shows that the observed slow plastic deformation is due to dislocation activity. Our results also...
متن کاملDislocation Processes and Deformation Behavior in <001>-Oriented FeX-Ni60â•fiX-Al40 Single Crystals
The mechanical properties and dislocation microstructure of single crystals with a range of compositions within the Fex-Ni60–x-Al40 pseudobinary system have been investigated, with the purpose of bridging the behavior from FeAl to NiAl. Experiments are focused on the compression testing of <001> oriented single crystals with compositions where x = 10, 20, 30, 40, and 50 (in atomic percent). Obs...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2010
ISSN: 1742-6596
DOI: 10.1088/1742-6596/240/1/012026