Hot Deformation Behavior and Pulse Current Auxiliary Isothermal Forging of Hot Pressing Sintering TiAl Based Alloys
This paper focuses on the fabrication of as-forged Ti46.5Al2Cr1.8Nb-(W, B) alloy via pulse current auxiliary isothermal forging (PCIF). The starting material composed of near gamma (NG) microstructure was fabricated by adopting pre-alloyed powders via hot pressing sintering (HPS) at 1300 °C. Isothermal compression tests were conducted at a strain rate range of 0.001-0.1 s-1 and a temperature ra...
متن کاملAbnormal deformation behavior in Polysynthetically-twinned TiAl crystals with A and N orientations ---- an AFM study
Polysynthetically-twinned TiAl crystals were deformed by compression with loading axis parallel and perpendicular to the lamellar interfaces. The deformation structures on the free surfaces were scanned using a dimension AFM with scan directions parallel and perpendicular to the lamellar interfaces. Abnormal deformation behaviors were observed to occur in both orientations. When the compression...
متن کاملFracture and Deformation
The high-velocity impact resistance of hot-pressed zirconum diboride with 30 volume percent silicon carbide was studied using a combined experimental and computational approach. Test specimens in the form of 2 mm thick polished disks were impacted with -0.8 mm diameter tungsten carbide spheres at velocities up to 320 d s . The intrinsic flexure strength of the specimens was -1000 MPa. The flexu...
متن کاملinvestigation of gassing behavior, electric and dielectric properties of different insulating fluids.
ترانسفورماتورهای قدرت از اجزای اصلی شبکه تامین انرژی الکتریکی می باشند که عملکرد قابل اطمینان ترانسفورماتورها یکی از فاکتورهای مهم و تعیین کننده در تامین انرژی الکتریکی محسوب می شود. در نتیجه بررسی و مانیتور عملکرد ترانسفورماتورها در شبکه و همچنین عیب یابی این ترانسفورماتورها غیرقابل اجتناب و ضروری می باشد. به طور کلی عایق های مایع در صنعت فشار قوی کاربردهای متفاوتی دارند که مهمترین وظیفه آنها...
15 صفحه اولEffects of Carbon on the Microstructure and Hot Deformation Behavior
The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite reg...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MRS Proceedings
سال: 1990
ISSN: 0272-9172,1946-4274
DOI: 10.1557/proc-186-265