Defect properties of vanadium doped barium titanate ceramics
نویسندگان
چکیده
منابع مشابه
Effect of re-oxidation firing on PTCR properties of Sm-doped barium titanate ceramics
The effect of reduction and re-oxidation firing on the PTCR properties of Sm-doped barium titanate ceramics was investigated for the application in multilayered PTC thermistors. The lattice parameters a, and c decreases monotonically with increasing oxygen concentration in the re-oxidation atmosphere, which seems to be related with an electrostatic Coulomb interaction between an oxygen vacancy ...
متن کاملDc and Ac Electrical Properties of Ptc Barium Titanate Ceramics
The dc and ac electrical properties of PTC barium titanate ceramics were measured in the temperature range from 30 to 450°C. The Heywang's model alone is not sufficient to perform a quantitative analysis of the results. The heterogeneity of the system is taken into account.
متن کاملSynthesis of Barium-zinc-titanate Ceramics
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered at 1250 °C for 2h with a heating rate of 10 °C/min. X-ray diffraction analysis of obtained powders and sintered samples was performed in order to investigate changes of the pha...
متن کاملBarium titanate as a ferroelectric and piezoelectric ceramics
Barium titanate is a member of a large family of compounds with the general formula ABO3 called perovskites, as the crystal size of barium titanate increases and at critical crystalline size crystal structure of barium titanate transformed from cubic to tetragonal. Transformation of crystal structure is also take place at Curi temperature. Cubic structure show paramagenatic behavior while tetra...
متن کاملCrystalline Structure, Defect Chemistry and Room Temperature Colossal Permittivity of Nd-doped Barium Titanate
Dielectric materials with high permittivity are strongly demanded for various technological applications. While polarization inherently exists in ferroelectric barium titanate (BaTiO3), its high permittivity can only be achieved by chemical and/or structural modification. Here, we report the room-temperature colossal permittivity (~760,000) obtained in xNd: BaTiO3 (x = 0.5 mol%) ceramics derive...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research Express
سال: 2019
ISSN: 2053-1591
DOI: 10.1088/2053-1591/ab4455