Decarburization from Molten Steel by Oxygen
نویسندگان
چکیده
منابع مشابه
Effects of Temperature and Oxygen Concentration on the Characteristics of Decarburization of 55SiCr Spring Steel
Effects of temperature and oxygen concentration on decarburization of 55SiCr spring steel were investigated at the temperature range of 500°C–1 200°C by using a Muffle furnace (an atmosphere of ambient air) and a Simultaneous Thermal Analyzer (low oxygen concentration with 2% O2 and 98% N2). In ambient air, the decarburization behavior can be divided roughly into five temperature ranges: T≥1 20...
متن کاملMeasurement of Decarburization of Heat Treated Steel Surfaces
Decarburization is a significant problem in the heat treatment of steels as decarburization is detrimental to wear life and fatigue life of components. This presentation concentrates on its measurement by four procedures. Test results from an interlaboratory test of steels with spheroidize annealed, lamellar pearlite (normalized) and quenched and tempered martensitic microstructures were evalua...
متن کاملHybrid Molten/Solid In2O3-Bi2O3 Oxygen Ion Transport Membranes
The hybrid molten/solid In2O3 - 30-48 wt.% Bi2O3 oxide materials were studied with respect to their transport properties. The conductivities, oxygen ion transport numbers and oxygen permeation fluxes have been measured by using the four-probe DC, volumetric measurements of the faradaic efficiency and gas flow techniques, respectively. We show that the...
متن کاملMultilayer perceptron to model the decarburization process in stainless steel production
The Argon-Oxygen Decarburization (AOD) is the refining process of stainless steel to get its final chemical composition through several stages, where tons of materials are added and oxygen and inert gas are blown. The decarburization efficiency and the final temperature in each stage are two important values of this process. We present in this paper an empirical model, based on Multilayer Perce...
متن کاملRemoval of MnS inclusions in molten steel using electropulsing
A method using electropulsing to separate inclusions from molten steel is developed, based on the differences in electrical properties between the inclusions and liquid metal. The inclusions have different electrical resistivity from that of the liquid steel and hence being expelled to the surface of the metal by electropulsing. In comparison with the as-solidified untreated steel, the size of ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1967
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.53.7_766