Damping Capacity and Pitting Corrosion Resistance of Fe–Mo–Cr Alloys
نویسندگان
چکیده
منابع مشابه
Pitting Resistance of Pure Fe-17%Cr Alloys: Consequences for Localized Corrosion Modeling
Pitting corrosion was observed on a high purity Fe-17Cr alloy in 0.02M NaCl solution of pH 6.6 at high anodic potential (+ 550 mVISCE). Potentiostatic electrochemical noise measurements were performed, revealing the presence of a characteristic current noise below stable pitting, differing strongly from that observed 011 a series of AISI 430 type 17% Cr stainless steels, with respect to the fre...
متن کاملCorrosion Resistance of Dental Alloys
Metals and metallic alloys are unavoidable materials in everyday dental use for the making of fillings, cast cores and post systems, individual crowns, implantants’ suprastructures, dentures and orthodontic devices. They still belong to the vital materials in dentistry. Applied alloys in a mouth are exposed to the influence of chemical, biological, mechanical, thermal and electrical forces whic...
متن کاملTarnish Resistance, Corrosion and Stress Corrosion Cracking of Gold Alloys
Tarnishing, corrosion and stress corrosion cracking (SeC) of gold alloys are related phenomena. They present problems when they occur in gold jewellery, dental gold alloys and electronic devices. They are exploited, however, in the depletion gilding and finishing of gold jewellery; and in the extraction, refining and fire assaying of gold. There is still much that is not known about these pheno...
متن کاملTHE ROLE OF ALKALINE CLEANING SOLUTIONS AND CL-CONTAINING LUBRICANTS ON PITTING CORROSION IN NiTi ALLOYS
Alkaline cleaning agents are found to react with remnant manufacturing lubricants trapped in surface defects of a NiTi alloy to form Cl-based salts. These sub-surface “reservoirs” may act as nucleation sites for pitting corrosion either latent under ambient conditions, or on exposure to a limited range of high temperatures used to impart pseudoelastic properties in these alloys as part of norma...
متن کاملPitting Corrosion of Heat-treatable Aluminium Alloys and Welds: a Reveiw
This review attempts to present the current understanding of the mechanism of pitting corrosion of heat treatable aluminium alloys and their welds. The role of alloying elements and intermetallic phases on the corrosion behavior of these alloys has been discussed. Pitting mechanism of aluminiumcopper alloys is specifically discussed. Finally effect of welding on the pitting corrosion of these a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Japan Institute of Metals
سال: 1984
ISSN: 0021-4434,2432-4701
DOI: 10.2320/matertrans1960.25.891