Damage monitoring of surface treated steel under severe rolling contact loading conditions
نویسندگان
چکیده
منابع مشابه
Analysis of Surface Crack Growth under Rolling Contact Fatigue
Understanding the fatigue crack growth phenomenon in railheads requires a study of driving forces such as the crack tip opening and sliding displacements, under repeated rolling contact. Finite element simulations, allowing elastic-plastic deformation, and mixed-mode crack growth laws were utilized to demonstrate that the fatigue crack growth rates display a minimum after a finite amount of cra...
متن کاملEffect of Surface Texturing on Cast Iron Reciprocating against Steel under Cyclic Loading in Boundary and Mixed Lubrication Conditions
This study investigates the effect of laser surface texturing on the friction behavior of grey cast iron reciprocating under boundary, mixed lubrication conditions and cyclic loading. Four geometrical parameters of micro-textures (feature depth, feature diameter, area fraction, and sliding direction) were studied using a design of experiments (DoE) approach. The results showed that depending on...
متن کاملImproved Method of Rolling Bearing Fatigue Life Prediction Under Edge Loading Conditions
More than half a century has passed since Lundberg and Palmgren (referred to as LP in the following) established a theory on the life of rolling bearings 1) 2), and problems with the theory such as its lack of capability of considering shear force (tangential force) on the surface caused by slip or the initial or residual stress due to fit have been pointed out, with correction to these problem...
متن کاملAnalysis of Keratin Fibre Damage under Various Surface Treatment Conditions
This paper investigates the effect of three different treatments, namely (i) sunlight exposures, (ii) bleaching and (iii) perming on the damage of the keratin fibres (with the use of human hair). Scanning electron microscopy was applied to examine the surface morphology of the samples. Hair samples appeared to be rougher and their scales diminished after the treatments. The degree of colour cha...
متن کاملFatigue strength evaluation of self-piercing riveted cold rolled steel joints under mixed mode loading conditions
Fatigue strength of cross-shaped specimens of SPR joints made of SPCC was evaluated at load angles of 0°, 45°, and 90°. For the static strength at load angles of 0°, 45°, and 90°, the maximum loads were determined to be 4890N, 1969N, and 1611N, respectively. Regarding for the relationship between the load amplitude and the number of cycles (Nf), the results were 014 . 0 3 . 2209 − = f amp N P ,...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tribology International
سال: 2020
ISSN: 0301-679X
DOI: 10.1016/j.triboint.2020.106257