Damage Evolution of Concrete Exposed to Sulfate Attack Under Drying-Wetting Cycles
نویسندگان
چکیده
منابع مشابه
Damage Evolution of Concrete Exposed to Sulfate Attack Under Drying- Wetting Cycles
The damage evolution of concrete subjected to drying-wetting cycles in different concentration of sodium sulfate solution was investigated based on micro and macro-observations. Through the experiment, weight loss, compressive strength loss and the damage layer thickness of concrete were measured after different drying-wetting cycles. The mechanical properties degradation in the damage layer of...
متن کاملPotassium status of two clayey calcareous soils treated with zeolite under wetting-drying cycles
Zeolite application to clayey soils may change potassium (K) pools distribution and its release rate. To test this hypothesis, two heavy-textured calcareous soils with different mineralogy (smectitic and mixed by XRD) from southern Iran were selected. Experiment was a completely randomized factorial arrangement. Treatments consisted of two soils and two zeolite levels (0 and 5%) and wetting-dry...
متن کاملCan drying and re-wetting of magnesium sulfate salts lead to damage of stone?
Magnesium sulfate salts have been linked to the decay of stone in the field and in laboratory experiments, but the mechanism of damage is still poorly understood. Thermomechanical analysis shows that expansion of stone contaminated with magnesium sulfate salts occurs during drying, followed by relaxation of the stress during dehydration of the precipitated salts. We applied thermogravimetric an...
متن کاملScaling and saturation laws for the expansion of concrete exposed to sulfate attack.
Reinforced concrete structures exposed to aggressive environments often require repair or retrofit even though they were designed to last >50 years. This statement is especially true for structures subjected to sulfate attack. It is critical that fundamental models of life prediction be developed for durability of concrete. Based on experimental results obtained over a 40-year period, scaling a...
متن کاملBehavior of engineered wood materials under the effect of wetting and drying cycles
A test procedure to simulate and measure the actual behavior of solid and engineered wood products subjected to realistic cyclic moisture loading conditions was carried out at the Institute for Research in Construction (IRC), National Research Council Canada (NRC). The wetting and drying experiments on oriented strand board (OSB), showed that the rate of moisture absorption and the rate of dryi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Open Construction and Building Technology Journal
سال: 2014
ISSN: 1874-8368
DOI: 10.2174/1874836801408010444