Cyclic deformation and fatigue of rolled AZ80 magnesium alloy along different material orientations

Kinetics of SIMA AZ80 Magnesium Alloy

Semi-solid feedstock of AZ80 magnesium alloy modified by [trace] rare-earth Y element 10 (0, 0.2, 0.4, 0.8 wt.%) were fabricated by [strain-induced melting activation] (SIMA) in the form of 11 extrusion and partial remelting. The effect of Y addition on the microstructure evolution of [the] 12 extruded and [isothermally heat] treated alloy was observed by [using an] optical microscope (OM), 13 ...

Fatigue and Anisotropic behaviours of cold rolled AA1200 Aluminium Alloy

This study examines the fatigue and anisotropy behaviour of cold rolled AA1200 aluminium alloy for light weight automotive connecting rod application. Aluminium (Al) 1200 ingots were melted at temperature of 680 0C (after one hour of heating) cast in sand mould and cast samples homogenized for 6 hrs at 480 0C. The cold rolling process was carried out after homogenisation for 10, 20, 30, 40 and ...

Hardness evolution of AZ80 magnesium alloy processed by HPT at different temperatures

Discs of an extruded AZ80 magnesium alloy were processed by high-pressure torsion (HPT) using 6.0 GPa up to 10 turns at different temperatures (296 K and 473 K). The disc surfaces and cross-sectional planes were examined before and after processing using scanning electron microscopy (SEM) and Vickers microhardness (Hv). The microhardness results at the surface show differences in the strength o...

Microstructure-sensitive investigation of magnesium alloy fatigue

THE DEFORMATION BEHAVIOR OF AZ31 MAGNESIUM ALLOY AT ELEVATED TEMPERATURES

AZ31 magnesium alloy is considered as a promising alloy in various applications and industries. Furthermore, to design a proper hot working process (rolling, forging and extrusion), the assessment of hot working behaviour of the alloy is necessary. Accordingly, the hot deformation behaviour of AZ31 alloy was studied through hot compression testing method This was carried out in a wide range of ...