Current Annealings and Magnetoimpedance in Co-Fe Amorphous Ribbons

Composition dependence of field induced anisotropy in ferromagnetic „Co,Fe...89Zr7B4 and „Co,Fe...88Zr7B4Cu1 amorphous and nanocrystalline ribbons

The composition dependence of field induced anisotropy KU of field annealed soft ferromagnetic Co1−xFex 89Zr7B4 and Co1−xFex 88Zr7B4Cu1 amorphous and amorphous/nanocrystalline “nanocomposite” melt spun ribbons is investigated. With the exception of the highest Co-containing alloys x 0.10 , the observations are discussed in terms of a superposition of directional pair ordering of Fe,Co atoms and...

Temperature stability of field induced anisotropy in soft ferromagnetic Fe,Co-based amorphous and nanocomposite ribbons

The temperature stability of field induced uniaxial anisotropy KU was investigated by thermomagnetic treatments of Co1−xFex 89Zr7B4 amorphous ribbons after field annealing below and above the crystallization temperature. We conclude: 1 Field annealing treatments are necessary to properly investigate the temperature stability of KU, 2 KU of field crystallized alloys exhibit improved temperature ...

Longitudinally driven giant magnetoimpedance effect in stress-annealed Fe-based nanocrystalline ribbons

A high-frequency longitudinally driven giant magnetoimpedance ~GMI! effect has been measured in stress-annealed Fe73Cu1Nb1.5V2Si13.5B9 nanocrystalline ribbons. Based on how the impedance phase varies with the external magnetic field, it becomes clear that the imaginary part of the complex permeability, m9, which is related to magnetic losses, plays an important role in the high-frequency longit...

Properties using metallic amorphous ribbons from (Fe-Co-Ni)- metalloid system, obtained by melt-quenching

Nanocrystallization in Co67Cr7Fe4Si8B14 Amorphous Alloy Ribbons

The nanocrystallization of Co67Fe4Cr7Si8B14 amorphous ribbons which prepared by planar flow melt spinning process (PFMS) was investigated. Crystallization of the ribbons was studied by differential thermal analysis (DTA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The DTA result of amorphous ribbon at heating rate of 10˚C/min showedoccurrence of phase transitions in two...