Crystallographic Texture of Induction-Welded and Heat-Treated Pipeline Steel
نویسندگان
چکیده
منابع مشابه
Crystallographic Texture of Induction-welded and Heat-treated Pipeline Steel
The Charpy energy of the sample after heat–treatment was significantly higher than the as–welded sample when the V–notches were located 1 or 3 mm away from FL. However, when the V–notch was located on FL, the improvement in toughness from the heat treatment was not so obvious with no enhancement noted for the test temperature of −40 ◦C. Under this condition, the facets of the fracture surface a...
متن کاملMicrostructure and Crystallographic Texture Characterization of Friction Stir Welded Thin AA2024 Aluminum Alloy
Friction stir welding (FSW) is a promising technique to join aluminum alloys without having problems encountered during fusion welding processes. In the present work, the evolution of microstructure and texture in friction stir welded thin AA2024 aluminum alloy are examined by electron backscattered diffraction (EBSD) technique. The sheets with 0.8 mm thickness were successfully welded by frict...
متن کاملFatigue Assessment of Complex Welded Steel Structures
To improve the usage of material in fatigue loaded complex welded structures a better calculation method (based on FEA) is needed than what is available on the market and an improved management of weld quality. Improved FE-procedures are directly applicable to design of generic structural components within virtually all industries using CAD and FEtools, irrespective of industrial sector. More a...
متن کاملCold End Forming Of Welded Steel Tubes
The production of custom and specific tube end shapes by cold end forming using a die is generally limited to seamless tubular parts. Current research work in the field follows the same trend as that of industry and, therefore, there is no accumulated experience, no practical design rules, and no information available in the specialized literature concerning the utilization of tube end forming ...
متن کاملMicrostructural Investigation of the Heat-affected Zone of Simulated Welded Joint of P91 Steel
T. Vuherer, University of Maribor, Faculty of Mechanical Engineering, Slovenia, M. Dunđer, University of Rijeka, Politechnika Department of Philosophy Faculty, Croatia, I. Samardžić, University of Osijek, Mechanical Engineering Faculty, Slav. Brod, Croatia, Lj. Milović, University of Belgrade, Faculty of Technology and Metallurgy, Serbia, M. Zrilić, University of Belgrade, Faculty of Technology...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advanced Materials Research
سال: 2010
ISSN: 1662-8985
DOI: 10.4028/www.scientific.net/amr.89-91.651