Crystallization of Cu60Zr20Ti20 bulk metallic glass by high pressure torsion

Polyamorphism of a Ce-based bulk metallic glass by high-pressure and high-temperature density measurements

Strain rate induced crystallization in bulk metallic glass-forming liquid.

We report on the solidification of Au49, Ag5.5, Pd2.3, Cu26.9, Si16.3 bulk metallic glass under various strain rates. Using a copper mold casting technique with a low strain rate during solidification, this alloy is capable of forming glassy rods of at least 5 mm in diameter. Surprisingly, when the liquid alloy is splat cooled at much higher cooling rates and large strain rates, the solidified ...

Mechanically driven phase separation and corresponding microhardness change in Cu60Zr20Ti20 bulk metallic glass

Ductile bulk metallic glass.

We report on experimental evidence of pronounced global plasticity measured in monolithic Pt57.5Cu14.7Ni5.3P22.5 bulk metallic glass under both bending and unconfined compression loading conditions. A plastic strain of 20% is measured, never before seen in metallic glasses. Also, permanent deformation and a strain exceeding 3% before failure is observed during bending of 4 mm thick samples. To ...

Pressure-dependent flow behavior of Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass

An experimental study of the inelastic deformation of bulk metallic glass Zr41.2Ti13.8Cu12.5Ni10Be22.5 under multiaxial compression using a confining sleeve technique is presented. In contrast to the catastrophic shear failure (brittle) in uniaxial compression, the metallic glass exhibited large inelastic deformation of more than 10% under confinement, demonstrating the nature of ductile deform...