Crystallization Behavior and Structural Stability of Zr_{50}Cu_{40}Al_{10} Bulk Metallic Glass
We have investigated the origin of significantly high thermal stability of Zr50Cu40Al10 metallic glass and its crystallization behavior as compared to Zr70Cu20Al10 and Zr70Cu30 glassy alloys, by differential scanning calorimetry (DSC), x-ray diffraction (XRD) and resonant ultrasound spectroscopy (RUS) techniques. It was found from XRD and DSC analyses that (i) constituent atoms in Zr50Cu40Al10 ...
متن کاملStructural relaxation of Ti40Zr25Ni8Cu9Be18 bulk metallic glass
The enthalpy relaxation behavior of Ti40Zr25Ni8Cu9Be18 bulk metallic glass follows the general characteristics of that for amorphous materials although its unique quenched-in nuclei/amorphous matrix structure: the annealing time dependence of recovery enthalpy follows a stretched exponential function with the mean relaxation time obeying an Arrhenius law, which may be due to the longer incubati...
متن کاملStrain rate induced crystallization in bulk metallic glass-forming liquid.
We report on the solidification of Au49, Ag5.5, Pd2.3, Cu26.9, Si16.3 bulk metallic glass under various strain rates. Using a copper mold casting technique with a low strain rate during solidification, this alloy is capable of forming glassy rods of at least 5 mm in diameter. Surprisingly, when the liquid alloy is splat cooled at much higher cooling rates and large strain rates, the solidified ...
متن کاملStructural and Mechanical Characterization of Zr58.5Ti8.2Cu14.2Ni11.4Al7.7 Bulk Metallic Glass
Thermal stability, structure and mechanical properties of the multi-component Zr58.5Ti8.2Cu14.2Ni11.4Al7.7 bulk metallic glass have been studied in detail. The glassy material displays good thermal stability against crystallization and a fairly large supercooled liquid region of 52 K. During heating, the alloy transforms into a metastable icosahedral quasicrystalline phase in the first stage of...
متن کاملMechanical performance and fracture behavior of Fe41Co7Cr15Mo14Y2C15B6 bulk metallic glass
The mechanical properties of a new Fe41Co7Cr15Mo14Y2C15B6 bulk glassy alloy were studied by impact bending, compression, and hardness tests carried out at room temperature. The compressive fracture strength, elastic strain to fracture, Young’s modulus and Vickers hardness were measured to be 3.5 GPa, 1.5%, 265 GPa, and 1253 kg mm, respectively. The fracture mode of the glassy alloy under uniaxi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATERIALS TRANSACTIONS
سال: 2009
ISSN: 1345-9678,1347-5320
DOI: 10.2320/matertrans.mbw200833