Crystal growth and spectral properties of (Yb0.15Lu0.85xY0.85-0.85x)3Al5O12 single crystals
نویسندگان
چکیده
Four single crystals (Yb0.15Lu0.85xY0.85-0.85x)3Al5O12 (x = 0, 0.25, 0.5, 1) were grown by the Czochralski method. The correlation of host atom Lu:Y ratios with density and luminescence properties revealed. increases linearly increasing Lu3+ content, which will improve gamma ray cut-off ability. integrated intensity X-ray excited spectrum exponentially Y:Lu ratio, while decay time becomes even shorter content. These results provide a basis to balance comprehensive match different application requirements.
منابع مشابه
Magneto-Optical properties of GaP single crystal
The temperature dependence of magneto-optical and magneto-photoconductivity measurements were carried out in the range of (200-330) K. A home made optical cryostat was used for the measurements. The measured room temperature value of the energy gap was found to be 2.211 eV. The temperature coefficient of energy gap was found to be -5.48×10-4 eV/K obtained by the optical absorption method and -4...
متن کاملCrystal growth, structure and physical properties of crystals
Vesuvianite is an ortho-diorthosilicate of a general schematic formula X~19Y13Z18O68W10, where X – Ca and other cations, which occupy sites of coordination number 8, Y – cations occupying octahedrons and pentagonal polyhedrons: Al, Fe, Mg, Ti, etc., Z – Si in tetrahedrons, W – univalent and bivalent anions. Structures of vesuvianites are studied in dependence on a character of cation ordering i...
متن کاملGrowth, Mechanical, Thermal and Spectral Properties of Cr3+∶MgMoO4 Crystal
This paper reports the growth, mechanical, thermal and spectral properties of Cr(3+):MgMoO(4) crystals. The Cr(3+):MgMoO(4) crystals with dimensions up to 30 mm×18 mm×14 mm were obtained by TSSG method. The absorption cross-sections of (4)A(2)→(4)T(1) and (4)A(2)→(4)T(2) transitions are 12.94×10(-20) cm(2) at 493 nm and 7.89×10(-20) cm(2) at 705 nm for E//N(g), respectively. The Cr(3+):MgMoO(4)...
متن کاملGrowth and Properties of Single Crystals of Noncentrosymmetric Na3VO2B6O11
Anew nonlinear optical crystal, Na3VO2B6O11, has been grown by the top-seeded solution growthmethod using a Na2CO3-V2O5 flux. The structure of the compound was determined by single-crystal X-ray diffraction. It crystallizes in the noncentrosymmetric orthorhombic system, space groupP212121, with cell parameters a=7.7359(9) Å, b=10.1884(12) Å, c= 12.5697(15) Å, V= 990.7(2) Å, and Z= 4. Na3VO2B6O1...
متن کاملDetermination of Crystal Growth Rate and Morphology of Barium Carbonate Crystals in a Semi-batch Crystallizer
A semi-batch crystallization system is used to determine growth kinetics and morphology of barium carbonate crystals, under a constant pH value and constant temperature in the various relative supersaturations. Results show that crystal growth rate satisfies a first-order kinetic expression at high relative supersaturation, while at relative supersaturation values lower than 3, the k...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Chinese Optics Letters
سال: 2022
ISSN: ['1671-7694']
DOI: https://doi.org/10.3788/col202220.121601