Cryogenic in situ microcompression testing of Sn
نویسندگان
چکیده
منابع مشابه
Fully Submerged Composite Cryogenic Testing
1 General Introduction New methods for marine salvage and decommissioning of structures in the open sea are continually being sought in order to improve control and lower operational costs [1]. The concept design of a lightweight, cryogenic, marine, heavy lift, buoyancy system has been investigated [2]. The objective is to be able to raise or lower high mass objects controlled solely from a sur...
متن کاملIn-situ MEMS Testing
Related to the dramatically smaller volume of microelectromecanical systems (MEMS), new methods in testing and qualification are needed. On single crystal silicon (SCSi) based devices, stress and loading in operation introduces defects during the MEMS life time and increases the risk of failure. Reliability studies on potential failure sources have an impact on MEMS design and are essential to ...
متن کاملIn situ tensile testing of tin (Sn) whiskers in a focused ion beam (FIB)/scanning electron microscope (SEM)
Article history: Received 22 May 2017 Received in revised form 7 July 2017 Accepted 8 July 2017 Available online 19 July 2017 Tin and tin-alloyed electroplated films are known to be susceptible to whisker growth under a range of conditions,manyofwhich result in the generation of compressive stresses in thefilm. Compressive stress is considered to be one of the primary causes for whisker nucleat...
متن کاملFirst Cryogenic Testing of the ATLAS Superconducting Prototype Magnets
The superconducting magnet system of the ATLAS detector will consist of a central solenoid, two end-cap toroids and the barrel toroid made of eight coils (BT) symmetrically placed around the central axis of the detector. All these magnets will be individually tested in an experimental area prior to their final installation in the underground cavern of the LHC collider. A dedicated cryogenic tes...
متن کاملMicrocompression study of Al-Nb nanoscale multilayers
Microcompression tests were performed on the Al/Nb multilayers of incoherent interfaces with the layer thicknesses of 5 nm Al/5 nm Nb and 50 nm Al/50 nm Nb. The Al-Nb multilayers showed increase in strength as the layer thickness was reduced; the average flow stresses at 5% plastic strain from the 5 nm Al/5 nm Nb and 50 nm Al/50 nm Nb layer thickness specimens were determined to be 2.1 GPa and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Materialia
سال: 2014
ISSN: 1359-6454
DOI: 10.1016/j.actamat.2014.06.026