Cryo‐3D Printing of Hierarchically Porous Polyhydroxymethylene Scaffolds for Hard Tissue Regeneration
نویسندگان
چکیده
منابع مشابه
Hierarchically engineered fibrous scaffolds for bone regeneration.
Surface properties of biomaterials play a major role in the governing of cell functionalities. It is well known that mechanical, chemical and nanotopographic cues, for example, influence cell proliferation and differentiation. Here, we present a novel coating protocol to produce hierarchically engineered fibrous scaffolds with tailorable surface characteristics, which mimic bone extracellular m...
متن کاملPorous Biodegradable Metals for Hard Tissue Scaffolds: A Review
Scaffolds have been utilized in tissue regeneration to facilitate the formation and maturation of new tissues or organs where a balance between temporary mechanical support and mass transport (degradation and cell growth) is ideally achieved. Polymers have been widely chosen as tissue scaffolding material having a good combination of biodegradability, biocompatibility, and porous structure. Met...
متن کاملPorous ceramic bone scaffolds for vascularized bone tissue regeneration.
Hydroxyapatite scaffolds with a multi modal porosity designed for use in tissue engineering of vascularized bone graft substitutes were prepared by three dimensional printing. Depending on the ratio of coarse (mean particle size 50 microm) to fine powder (mean particle size 4 microm) in the powder granulate and the sintering temperature total porosity was varied from 30% to 64%. While macroscop...
متن کاملOvalbumin-Based Porous Scaffolds for Bone Tissue Regeneration
Cell differentiation on glutaraldehyde cross-linked ovalbumin scaffolds was the main focus of this research. Salt leaching and freeze drying were used to create a three-dimensional porous structure. Average pore size was 147.84 ± 40.36 μm and 111.79 ± 30.71 μm for surface and cross sectional area, respectively. Wet compressive strength and elastic modulus were 6.8 ± 3.6 kPa. Average glass trans...
متن کاملIbuprofen-Loaded CTS/nHA/nBG Scaffolds for the Applications of Hard Tissue Engineering
Background: This study addressed the development of biodegradable and biocompatible scaffolds with enhanced biomechanical characteristics. The biocompatibility and the cationic nature of chitosan (CTS) make it more effective as a bone grafting material. Methods: The hydroxyapatite nanoparticles (nHA) were synthesized by hydrothermal method, and bioglass (nBG) (50% SiO2-45% CaO-5% P2O5) was synt...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Macromolecular Materials and Engineering
سال: 2020
ISSN: 1438-7492,1439-2054
DOI: 10.1002/mame.202000541