Enhancement of the critical current density in FeO-coated MgB2 thin films at high magnetic fields
The effect of depositing FeO nanoparticles with a diameter of 10 nm onto the surface of MgB(2) thin films on the critical current density was studied in comparison with the case of uncoated MgB(2) thin films. We calculated the superconducting critical current densities (J(c)) from the magnetization hysteresis (M-H) curves for both sets of samples and found that the J(c) value of FeO-coated film...
متن کاملThermally activated current transport in MgB2 films
Thermally-activated flux flow (TAFF) resistivity above the irreversibility field Bi is reported for two different c-axis textured MgB2 superconducting films. Transport measurements at different perpendicular magnetic fields 0,B,9 T and temperatures from 5 to 40 K reveal TAFF Ohmic resistivity rsT ,Bd for B.Bi described by the Arrhenius law, r=r0 exps-U /Td with the quadratic field dependence of...
متن کاملEnhancement of the critical current density and flux pinning of MgB2 superconductor by nanoparticle SiC doping
Doping of MgB2 by nano-SiC and its potential for the improvement of flux pinning were studied for MgB22x(SiC)x/2 with x50, 0.2, and 0.3 and for 10 wt % nano-SiC-doped MgB2 samples. Cosubstitution of B by Si and C counterbalanced the effects of single-element doping, decreasing Tc by only 1.5 K, introducing intragrain pinning centers effective at high fields and temperatures, and significantly e...
متن کاملInfluence of Preparation Process on Microstructure, Critical Current Density and Tc of MgB2/Fe/Cu Wires
The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the dimple after post-heat treatment. The clear evidence for transcrystlline fracture is observed. It indicated that the grain connection was greatly improved and the...
متن کاملDramatic role of critical current anisotropy on flux avalanches in MgB2 films.
Anisotropic penetration of magnetic flux in MgB(2) films grown on vicinal sapphire substrates is investigated using magneto-optical imaging. Regular penetration above 10 K proceeds more easily along the substrate surface steps, the anisotropy of the critical current being 6%. At lower temperatures the penetration occurs via abrupt dendritic avalanches that preferentially propagate perpendicular...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied Physics Letters
سال: 2003
ISSN: 0003-6951,1077-3118
DOI: 10.1063/1.1590734