Critical condition parameters and kinetics of dynamic recrystallization for hot deformed 1 wt%Cr-1 wt%Mo rotor steel
نویسندگان
چکیده
منابع مشابه
Dynamic recrystallization kinetics of AISI 403 stainless steel using hot compression test
In this work dynamic recrystallization behavior of AISI 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 C -1200 C and strain rate range of 0.001 s-1 - 1 s-1. The obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. The flow stress and strain corresponding to the critical, pe...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملDynamic Recrystallization and Hot Workability of 316LN Stainless Steel
Chaoyang Sun 1,*, Yu Xiang 1, Qingjun Zhou 2, Denis J. Politis 3, Zhihui Sun 1,* and Mengqi Wang 1 1 School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083, China; [email protected] (Y.X.); [email protected] (M.W.) 2 Capital Aerospace Machinery Company, Beijing 100076, China; [email protected] 3 Department of Mechanical Engineering, Imperial Co...
متن کاملdynamic recrystallization kinetics of aisi 403 stainless steel using hot compression test
in this work dynamic recrystallization behavior of aisi 403 martensitic stainless steel was studied using hot compression tests over temperature range of 900 c -1200 c and strain rate range of 0.001 s-1 - 1 s-1. the obtained flow curves showed that the hot compression behavior of the alloy is controlled by dynamic recrystallization. the flow stress and strain corresponding to the critical, pe...
متن کاملdynamic recrystallization under hot deformation of a ph stainless steel
dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Research Express
سال: 2020
ISSN: 2053-1591
DOI: 10.1088/2053-1591/ab731b