The Role of Alloying Elements on the Crevice Corrosion Behavior of Ni-Cr-Mo Alloys
The roles of the alloying elements Mo, Cr, and W in resisting crevice corrosion of UNS N06022, UNS N06625, and UNS N10362 have been studied under galvanostatic conditions in 5 mol/L NaCl at 150°C. Corrosion damage patterns were investigated using surface analytical techniques such as scanning electron microscopy and optical imaging, and the corrosion products characterized by energy dispersive ...
متن کاملOxidation – Nitridation of Ni-Cr-Al Alloys
A series of alloys containing 24-36 wt pct Cr and 13.5 – 25.0 wt pct Al was reacted with air at 1100 °C for 260 h. The products of isothermal reaction were scales of α-Al 2 O 3 plus small amounts of Cr 2 O 3 . These grew according to parabolic kinetics, interrupted by episodic weight losses caused by partial spallation. No nitridation occurred during the isothermal exposures. Reaction during th...
متن کاملEvaluation on the Corrosion of the Three Ni-Cr Alloys with Different Composition
Dental casting alloys are widely used in contact with oral tissue for many years now. With the development of new dental alloys over the past 15 years, many questions remain unanswered about their biologic safety. Concepts and current issues concerning the response to the biologic effects of dental casting alloys are presented. In this paper, samples of three commercially available nickel-chrom...
متن کاملCorrosion performance of Ni-Cr-Fe alloys in geothermal hypersaline brines
The early development of the Salton Sea geothermal resource proved that carbon steel tubulars do not provide satisfactory service life in the high-temperature, hypersaline brines. A large-scale corrosion test was designed to find the most cost-effective alloys for completing these wells. A series of Ni-Cr-Mo alloys were tested over several years in three production wells and two injection wells...
متن کاملCorrosion Performance of Fe-Cr-Ni Alloys in Artificial Saliva and Mouthwash Solution
Several austenitic stainless steels suitable for high temperature applications because of their high corrosion resistance and excellent mechanical properties were investigated as biomaterials for dental use. The steels were evaluated by electrochemical techniques such as potentiodynamic polarization curves, cyclic polarization curves, measurements of open circuit potential, and linear polarizat...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ECS Transactions
سال: 2019
ISSN: 1938-6737
DOI: 10.1149/1.2789233