Creep-Fatigue Crack Growth Interaction in Nickel Base Supper Alloy
نویسندگان
چکیده
منابع مشابه
The Fracture Mechanics Concept of Creep and Creep/Fatigue Crack Growth in Life Assessment
There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...
متن کاملHigh frequency fatigue crack propagation behavior of a nickel-base turbine disk alloy
Fatigue crack propagation tests were conducted on the powder metallurgy nickel-base superalloy KM4 at room temperature. Two different heat treatments were investigated, one which produced a relatively coarse grain size around 55 μm, and another which produced a very fine grain size around 6 μm. Tests were conducted at 50 Hz and 1000 Hz in an advanced servohydraulic testing machine at R-ratios b...
متن کاملFatigue crack growth in a coarse-grained iron–silicon alloy
The fatigue crack growth in a coarse-grained Fe-2 wt% Si alloy is investigated in considerable detail. At room temperature, the material is quasi-brittle and the failure mode is mixed cleavage. Under a mode-I cyclic loading, the crack can overcome the barrier effect of grain boundaries, which dominates the overall damage evolution. Associated with the geometrically necessary crack front branchi...
متن کاملCreep Crack Growth Simulation of Ni-base Superalloy
The purpose of this study is to develop a numerical approach to simulate the creep cracking of a Ni-base superalloy. The approach is based in continuum damage mechanics (CDM) and uses the classic Kachanov-Rabotnov constitutive equations for creep deformation and damage evolution. Creep damage takes the form of defects such as microcracks, cavities, voids, etc. A numerical crack growth algorithm...
متن کاملAccelerated Threshold Fatigue Crack Growth Effect – Powder Metallurgy Aluminum Alloy
Fatigue crack growth (FCG) research conducted in the near threshold regime has identified a room temperature creep crack growth damage mechanism for a fine grain powder metallurgy (PM) aluminum alloy (8009). At very low ∆K, an abrupt acceleration in room temperature FCG rate occurs at high stress ratio (R = Kmin/Kmax). The near threshold accelerated FCG rates are exacerbated by increased levels...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: American Journal of Applied Sciences
سال: 2008
ISSN: 1546-9239
DOI: 10.3844/ajassp.2008.454.460