Creation of special compositions based on butadiene-nitrile elastomers for diesels

In the article, it was determined that furan oligomer added to composition causes additional structuring in process of vulcanization, and as a result, density hardness vulcanization network composite increases, value relative length decreases. It shown optimal amount oligomers rubber compounds is equal 10 weight units per 100 rubber. With inclusion secondary product acetylene production elastomer compositions, found carbon-rubber gel increased, level vulcanizate shrinkage decreased, which be mainly due presence oligomeric components on surface carbon particles. this raw material elastomeric compositions based butadiene nitrile increases interaction at “rubber-filler” boundary formation bonds between macromolecules functional groups oligomer, overall technological technical properties are improved.